Role of Re in NiAl bond coating on isothermal oxidation behavior of a thermal barrier coating system at 1100 degrees C
文献类型：期刊论文
| 作者 | Peng, X.1,2; Li, W.1; Fu, L. B.1; Li, Y. T.1,2; Jiang, S. M.1; Gong, J.1; Sun, C.1 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2023-07-01 |
| 卷号 | 218页码:11 |
| 关键词 | Thermal barrier coatings Rhenium Oxidation Superalloys Failure mode |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2023.111151 |
| 通讯作者 | Gong, J.(jgong@imr.ac.cn) ; Sun, C.(csun@imr.ac.cn) |
| 英文摘要 | Role of Re in NiAl bond coating on intermittent isothermal oxidation behavior of thermal barrier coatings (TBCs) was researched in this study. Isothermal oxidation behaviors of NiAl-YSZ coatings with and without Re were investigated at 1100 & DEG;C. Results showed that NiAlRe-YSZ coating revealed lower level of & beta; to & gamma;& PRIME; phase transformation, and less severe delamination of YSZ was observed compared with NiAl-YSZ coating after 300 h oxidation. Moreover, the synergistic effect of Re and Zr/Y jointly improved delamination resistance of NiAlReYSZ coating during oxidation. Severe internal oxidation and rumpling prompted the delamination of YSZ for NiAl-YSZ coating without Re. |
| 资助项目 | Key Research Program of the Chi-nese Academy of Sciences[2022-PY17] ; IMR Inno-vation Fund[P2021-A-IV-002-003] ; Science Center for Gas Turbine Project ; [ZDRW-CN-2021-2-2] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001053680000001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | Key Research Program of the Chi-nese Academy of Sciences ; IMR Inno-vation Fund ; Science Center for Gas Turbine Project |
| 源URL | [http://ir.imr.ac.cn/handle/321006/179062]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Gong, J.; Sun, C. |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Peng, X.,Li, W.,Fu, L. B.,et al. Role of Re in NiAl bond coating on isothermal oxidation behavior of a thermal barrier coating system at 1100 degrees C[J]. CORROSION SCIENCE,2023,218:11. |
| APA | Peng, X..,Li, W..,Fu, L. B..,Li, Y. T..,Jiang, S. M..,...&Sun, C..(2023).Role of Re in NiAl bond coating on isothermal oxidation behavior of a thermal barrier coating system at 1100 degrees C.CORROSION SCIENCE,218,11. |
| MLA | Peng, X.,et al."Role of Re in NiAl bond coating on isothermal oxidation behavior of a thermal barrier coating system at 1100 degrees C".CORROSION SCIENCE 218(2023):11. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。