Chlorine-induced high-temperature corrosion of the Pt-modified aluminide coating in simulated marine environment

文献类型：期刊论文

作者Li, Y. Y.1,2; Zhang, C.3; Niu, X. Y.3; Zhang, C. Y.4; Li, S.1; Bao, Z. B.1,2; Zhu, S. L.1,2; Wang, F. H.4
刊名CORROSION SCIENCE
出版日期2023-11-01
卷号224页码:11
关键词Pt-modified aluminide coating Cyclically alternate corrosion High-temperature corrosion Chlorination Water vapor
ISSN号0010-938X
DOI10.1016/j.corsci.2023.111493
通讯作者Li, S.(sli17s@imr.ac.cn) ; Bao, Z. B.(zbbao@imr.ac.cn)
英文摘要The corrosion behavior of a single phase Pt-modified aluminide coating in the marine environment was investigated through a novel cyclically alternate corrosion test. The results showed that the multilayer oxide scale with loose structure was formed on the coating. NaCl and water vapor were verified to play important roles in enhancing the aggressivity during the corrosion test, in which the presence of NaCl increased cracking and spallation tendency of the oxide scale, and the addition of water vapor accelerated the oxidation rate and promoted internal oxidation to the coating.
资助项目National Science and Technology Major Project[J2019 -IV -0006-0074] ; Key Research Program of the Chinese Academy of Sciences[ZDRW-CN-2021-2-2] ; Joint Funds of the National Natural Science Foundation of China[U2241251] ; Innovation Engineering Project[211-XXXX-N106-01]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
WOS记录号WOS:001072446000001
出版者PERGAMON-ELSEVIER SCIENCE LTD
资助机构National Science and Technology Major Project ; Key Research Program of the Chinese Academy of Sciences ; Joint Funds of the National Natural Science Foundation of China ; Innovation Engineering Project
源URL[http://ir.imr.ac.cn/handle/321006/179364]  
专题金属研究所_中国科学院金属研究所
通讯作者Li, S.; Bao, Z. B.
作者单位1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Wencui Rd 62, Shenyang 110016, Peoples R China
2.Univ Sci & Technol China, Sch Mat Sci & Engn, Wenhua Rd 72, Shenyang 110016, Peoples R China
3.703 Res Inst CSSC, Lab Ocean Engn Gas Turbine, Honghu Rd 31, Harbin 150078, Peoples R China
4.Northeastern Univ, Shenyang Natl Lab Mat Sci, Wenhua Rd 3, Shenyang 110819, Peoples R China
推荐引用方式
GB/T 7714		 Li, Y. Y.,Zhang, C.,Niu, X. Y.,et al. Chlorine-induced high-temperature corrosion of the Pt-modified aluminide coating in simulated marine environment[J]. CORROSION SCIENCE,2023,224:11.
APA Li, Y. Y..,Zhang, C..,Niu, X. Y..,Zhang, C. Y..,Li, S..,...&Wang, F. H..(2023).Chlorine-induced high-temperature corrosion of the Pt-modified aluminide coating in simulated marine environment.CORROSION SCIENCE,224,11.
MLA Li, Y. Y.,et al."Chlorine-induced high-temperature corrosion of the Pt-modified aluminide coating in simulated marine environment".CORROSION SCIENCE 224(2023):11.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。