Temperature induced cathode-anode reversal behavior of TA2-304 L galvanic couple in simulated spent fuel reprocessing media
文献类型：期刊论文
| 作者 | Tan, K. D.1,2; Liu, Z.1,2; Zhang, L. M.2,3; Liu, C. C.2; Ma, A. L.2; Zheng, Y. G.2 |
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2023-11-10 |
| 卷号 | 468页码:13 |
| 关键词 | Galvanic corrosion Spent fuel reprocessing Electrochemical behavior Passive film characteristics Critical temperature |
| ISSN号 | 0013-4686 |
| DOI | 10.1016/j.electacta.2023.143168 |
| 通讯作者 | Zhang, L. M.(lmzhang14s@imr.ac.cn) ; Zheng, Y. G.(ygzheng@imr.ac.cn) |
| 英文摘要 | Galvanic corrosion is prevalent throughout various stages of spent fuel reprocessing, and plays a crucial role in the corrosion failure of equipment materials due to its pronounced local corrosive effects. Nevertheless, there is a scarcity of systematic investigations regarding the impact of temperature on the corrosion mechanism of galvanic couples in simulated spent fuel reprocessing media. This study aims to explore the electrochemical behavior and passive film characteristics of TA2-304 L galvanic couple immersed in nitric acid solutions at different temperatures. Relevant results indicated that temperature significantly affected the galvanic corrosion behavior of TA2-304 L couple in nitric acid. The galvanic couple demonstrated a notable reversal in cathodic and anodic polarity with the rising temperature, which was closely related to the changed corrosion mechanism of 304 L SS from superior passivation performance to severe intergranular corrosion. Meanwhile, a critical temperature phenomenon was observed for TA2, below which there exhibited a monotonically decreased corrosion resistance with the increase in temperature. However, an improved corrosion resistance was found as the temperature rose to 120 degrees C, which could be associated with the decreased oxidative properties of nitric acid because of the variation in electrochemical/chemical reactions. Additionally, the relationship between corrosion rate and temperature of both 304 L SS and TA2 was created, and the activation energy was calculated to stress the influence of temperature on the corrosion of both materials. Eventually, the galvanic mechanism of TA2-304 L couple with temperature in nitric acid was proposed. |
| 资助项目 | National Natural Science Foundation of China[52101105] ; National Natural Science Foundation of China[52373321] ; IMR Innovation Fund[2023-PY03] ; LingChuang Research Project of China National Nuclear Corporation[CNNC-LCKY-202274] |
| WOS研究方向 | Electrochemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:001080852700001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Natural Science Foundation of China ; IMR Innovation Fund ; LingChuang Research Project of China National Nuclear Corporation |
| 源URL | [http://ir.imr.ac.cn/handle/321006/179439]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, L. M.; Zheng, Y. G. |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, CAS Key Lab Nucl Mat & Safety Assessment, Inst Met Res, 62 Wencui Rd, Shenyang 110016, Peoples R China 3.Ecole Natl Super Chim Paris, Chim ParisTech, 11 Rue Pierre & Marie Curie, F-75005 Paris, France |
| 推荐引用方式 GB/T 7714 | Tan, K. D.,Liu, Z.,Zhang, L. M.,et al. Temperature induced cathode-anode reversal behavior of TA2-304 L galvanic couple in simulated spent fuel reprocessing media[J]. ELECTROCHIMICA ACTA,2023,468:13. |
| APA | Tan, K. D.,Liu, Z.,Zhang, L. M.,Liu, C. C.,Ma, A. L.,&Zheng, Y. G..(2023).Temperature induced cathode-anode reversal behavior of TA2-304 L galvanic couple in simulated spent fuel reprocessing media.ELECTROCHIMICA ACTA,468,13. |
| MLA | Tan, K. D.,et al."Temperature induced cathode-anode reversal behavior of TA2-304 L galvanic couple in simulated spent fuel reprocessing media".ELECTROCHIMICA ACTA 468(2023):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。