Study on hydrogen permeation and stress corrosion cracking behaviors of AISI 4135 high-strength steel with macrofouling adhesion in marine immersion zone
文献类型：期刊论文
| 作者 | Cai, Fanfan1,2,3 ; Huang, Yanliang1,3; Xu, Yong1,2,3; Xin, Yu1,2,3; Pu, Jiayan1,2,3; Liu, Xiangjv1,3; Wang, Xiutong1,3; Li, Yantao1,3; Yang, Lihui1,3
|
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2024-04-20 |
| 卷号 | 484页码:13 |
| 关键词 | High -strength steel Macrofouling adhesion Crevices Hydrogen permeation Stress corrosion cracking |
| ISSN号 | 0013-4686 |
| DOI | 10.1016/j.electacta.2024.144088 |
| 通讯作者 | Huang, Yanliang(hyl@qdio.ac.cn) |
| 英文摘要 | A field exposure test was set up to study the effect of macrofouling adhesion on hydrogen permeation and stress corrosion cracking (SCC) behaviors of a high-strength steel in marine immersion zone, and the results were further verified by laboratory electrochemical simulation tests. The results indicated that the crevices formed by macrofouling adhesion can promote localized corrosion pits and change the local chemical environment. More severe localized corrosion can increase the hydrogen permeation current density and promote the SCC of highstrength steel. As a comparison, the hydrogen permeation current density of steel under cathodic protection state was slightly decreased owing to the shielding effect of macrofouling. |
| WOS关键词 | DUPLEX STAINLESS-STEEL ; CATHODIC PROTECTION ; CREVICE CORROSION ; ATMOSPHERIC CORROSION ; LOCALIZED CORROSION ; PIPELINE STEEL ; CARBON-STEEL ; OXIDE-FILMS ; E690 STEEL ; X80 STEEL |
| 资助项目 | National Natural Science Foundation of China[42276211] ; National Natural Science Foundation of China[41976033] |
| WOS研究方向 | Electrochemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:001226847000001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/185796]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 通讯作者 | Huang, Yanliang |
| 作者单位 | 1.Chinese Acad Sci, Ctr Ocean Mega Sci, 7 Nanhai Rd, Qingdao 266071, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Cai, Fanfan,Huang, Yanliang,Xu, Yong,et al. Study on hydrogen permeation and stress corrosion cracking behaviors of AISI 4135 high-strength steel with macrofouling adhesion in marine immersion zone[J]. ELECTROCHIMICA ACTA,2024,484:13. |
| APA | Cai, Fanfan.,Huang, Yanliang.,Xu, Yong.,Xin, Yu.,Pu, Jiayan.,...&Yang, Lihui.(2024).Study on hydrogen permeation and stress corrosion cracking behaviors of AISI 4135 high-strength steel with macrofouling adhesion in marine immersion zone.ELECTROCHIMICA ACTA,484,13. |
| MLA | Cai, Fanfan,et al."Study on hydrogen permeation and stress corrosion cracking behaviors of AISI 4135 high-strength steel with macrofouling adhesion in marine immersion zone".ELECTROCHIMICA ACTA 484(2024):13. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。