Effects of MoO3 Amounts on Sintering and Electrical Properties of Ce0.8Nd0.2O1.9
文献类型：期刊论文
| 作者 | Zhou DF ; Zhao GC ; Yang M ; Xia YJ ; Meng J |
| 刊名 | chemical research in chinese universities
 |
| 出版日期 | 2012 |
| 卷号 | 28期号:1页码:9-13 |
| 关键词 | DOPED CERIA CE0.9GD0.1O2-DELTA CERAMICS OXALATE COPRECIPITATION SOLID-SOLUTIONS GRAIN-GROWTH ELECTROLYTES CONDUCTIVITY TEMPERATURE OXIDE CEO2 |
| ISSN号 | 1005-9040 |
| 通讯作者 | zhou df |
| 中文摘要 | the high purity (ce0.8nd0.2o1.9), (moo3),(x=0, 0.005, 0.010, 0.020; ce0.8nd0.2o1.9=ndc) solid solutions were prepared by modified sol-gel method. the structures and electric conductivities were characterized by x-ray diffraction(xrd), field-emission scanning electron microscopy(fesem) and electrochemical impedance spectroscopy(eis). the xrd results show that the materials were pure phase with a cubic fluorite structure. compared to the undoped-ndc samples, moo3 doped-ndc showed higher sintered density(over 96%) at reduced sintering temperature. the electric conductivity(sigma(1)) of (ce0.8nd0.2o1.9)(1-x)(moo3), at 400 degrees c was 9.58x10(-4) s/cm when x=0.010, which was higher than that of undoped-ndc samples(sigma(1)=3.29x10(-4) s/cm). the obtained optimal amount of the moo3 was x=0.010 in this system. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000300808300003 |
| 公开日期 | 2013-10-31 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/48882]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhou DF,Zhao GC,Yang M,et al. Effects of MoO3 Amounts on Sintering and Electrical Properties of Ce0.8Nd0.2O1.9[J]. chemical research in chinese universities,2012,28(1):9-13. |
| APA | Zhou DF,Zhao GC,Yang M,Xia YJ,&Meng J.(2012).Effects of MoO3 Amounts on Sintering and Electrical Properties of Ce0.8Nd0.2O1.9.chemical research in chinese universities,28(1),9-13. |
| MLA | Zhou DF,et al."Effects of MoO3 Amounts on Sintering and Electrical Properties of Ce0.8Nd0.2O1.9".chemical research in chinese universities 28.1(2012):9-13. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。