Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen
文献类型：期刊论文
| 作者 | Zhang, Zhiyuan1,2,3; Zhang, Zhiming3; Wang, Jianqiu1,2,3; Ming, Hongliang1,2; Zhu, Haipeng1,2; Han, En-Hou1,3,4 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2025-04-01 |
| 卷号 | 245页码:13 |
| 关键词 | Polyacrylic acid Alloy 690 Alloy 800 High-temperature water Dissolved oxygen Oxide film |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2025.112709 |
| 通讯作者 | Wang, Jianqiu(wangjianqiu@imr.ac.cn) |
| 英文摘要 | The corrosion behavior of Alloys 690 and 800 was investigated in high-temperature water containing dissolved oxygen (DO) and polyacrylic acid (PAA). DO caused Cr dissolution as HCrO4-, leading to the formation of Crdepleted oxide films on both alloys. Alloy 800, with higher Fe content, formed a more protective Ni-Fe spinel inner layer, while Alloy 690, with lower Fe content, formed a less protective NiO inner layer. The thermal degradation of PAA resulted in surface acidification, which accelerated Cr and Ni dissolution under DO, further intensifying corrosion. Under DO conditions, Alloy 800 exhibited superior oxidation resistance compared to Alloy 690, regardless of PAA presence. |
| 资助项目 | LingChuang Research Project of China National Nuclear Corporation ; Youth Innovation Promotion Association CAS[2022187] ; Testing Center of Institute of Corrosion Science and Technology |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001402719200001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | LingChuang Research Project of China National Nuclear Corporation ; Youth Innovation Promotion Association CAS ; Testing Center of Institute of Corrosion Science and Technology |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Jianqiu |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Inst Corros Sci & Technol, Guangzhou 510530, Peoples R China 4.South China Univ Technol, Sch Mat Sci & Engn, Guangzhou 510006, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Zhiyuan,Zhang, Zhiming,Wang, Jianqiu,et al. Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen[J]. CORROSION SCIENCE,2025,245:13. |
| APA | Zhang, Zhiyuan,Zhang, Zhiming,Wang, Jianqiu,Ming, Hongliang,Zhu, Haipeng,&Han, En-Hou.(2025).Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen.CORROSION SCIENCE,245,13. |
| MLA | Zhang, Zhiyuan,et al."Comparative corrosion behavior of Alloys 690 and 800 in high-temperature water: Combined effects of polyacrylic acid and dissolved oxygen".CORROSION SCIENCE 245(2025):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。