Revealing the Void Formation Mechanism during Superplastic Deformation of a Fine-Grained Ni-Co-Base Superalloy
文献类型：期刊论文
| 作者 | Al-Hammadi, Rashad A.1,2; Zhang, Rui1; Cui, Chuanyong1; Zhou, Zijian1; Zhou, Yizhou1 |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2024-02-12 |
| 页码 | 6 |
| 关键词 | Superplasticity Void formation Ni-Co-based superalloy Microstructure |
| ISSN号 | 1006-7191 |
| DOI | 10.1007/s40195-024-01670-8 |
| 通讯作者 | Zhang, Rui(rzhang@imr.ac.cn) ; Cui, Chuanyong(chycui@imr.ac.cn) |
| 英文摘要 | The mechanism behind void formation during superplasticity remains a subject of uncertainty. This study presented a novel insight into the void formation in a fine-grained Ni-Co-based superalloy during superplasticity. It was observed that the dissolution of gamma '-particles resulted in the creation of vacancies due to differences in atomic size between the matrix and the particles. These vacancies acted as inclusions, leading to the formation of micro-voids. Notably, excessive void formation correlated with higher particle dissolution was experimentally observed, highlighting a direct relationship between void formation and particle dissolution. |
| 资助项目 | National Key R&D Program of China[2019YFA0705300] ; Youth Innovation Promotion Association, CAS[2023202] ; Natural Science Foundation Project of Liaoning Province[2023-MS-024] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001161045100001 |
| 出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| 资助机构 | National Key R&D Program of China ; Youth Innovation Promotion Association, CAS ; Natural Science Foundation Project of Liaoning Province |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, Rui; Cui, Chuanyong |
| 作者单位 | 1.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Al-Hammadi, Rashad A.,Zhang, Rui,Cui, Chuanyong,et al. Revealing the Void Formation Mechanism during Superplastic Deformation of a Fine-Grained Ni-Co-Base Superalloy[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2024:6. |
| APA | Al-Hammadi, Rashad A.,Zhang, Rui,Cui, Chuanyong,Zhou, Zijian,&Zhou, Yizhou.(2024).Revealing the Void Formation Mechanism during Superplastic Deformation of a Fine-Grained Ni-Co-Base Superalloy.ACTA METALLURGICA SINICA-ENGLISH LETTERS,6. |
| MLA | Al-Hammadi, Rashad A.,et al."Revealing the Void Formation Mechanism during Superplastic Deformation of a Fine-Grained Ni-Co-Base Superalloy".ACTA METALLURGICA SINICA-ENGLISH LETTERS (2024):6. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。