Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water
文献类型：期刊论文
| 作者 | Qiao, Yufei1,2; Zheng, Hui3; Tan, Jibo1; Yang, Shuangliang3; Zhang, Ziyu1; Li, Jie3; Wu, Xinqiang1; Ke, Wei1 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2024-04-01 |
| 卷号 | 229页码:13 |
| 关键词 | Stainless steel Thermal aging Corrosion fatigue Ferrite High temperature corrosion |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2024.111869 |
| 通讯作者 | Tan, Jibo(jbtan10s@imr.ac.cn) |
| 英文摘要 | The effect of thermal aging (0 h- 15,000 h at 400 degrees C) on the low cycle fatigue properties of Z3CN20.09M stainless steel was investigated. The micro-hardness of the ferrite increases with thermal aging time, while that of the austenite is almost unchanged. The fatigue life of Z3CN20.09M stainless steel in high-temperature pressurized water decreases with thermal aging time. The fatigue cracks formed everywhere, mainly including at slip bands in austenite, at the delta/gamma phase boundary and in ferrite. Thermal aging promotes crack initiation and propagation in ferrite. The effect of thermal aging on the fatigue damage process is discussed. |
| 资助项目 | National Key Research and Development Program of China[2019YFB1900905] ; Youth Innovation Promotion Association CAS[2021189] ; CNNC Science Fund for Talented Young Scholars ; Xingliao Talent Plan of Liaoning Province |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001175169700001 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Key Research and Development Program of China ; Youth Innovation Promotion Association CAS ; CNNC Science Fund for Talented Young Scholars ; Xingliao Talent Plan of Liaoning Province |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Tan, Jibo |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 3.State Nucl Power Plant Serv Co, Shanghai 200233, Peoples R China |
| 推荐引用方式 GB/T 7714 | Qiao, Yufei,Zheng, Hui,Tan, Jibo,et al. Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water[J]. CORROSION SCIENCE,2024,229:13. |
| APA | Qiao, Yufei.,Zheng, Hui.,Tan, Jibo.,Yang, Shuangliang.,Zhang, Ziyu.,...&Ke, Wei.(2024).Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water.CORROSION SCIENCE,229,13. |
| MLA | Qiao, Yufei,et al."Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water".CORROSION SCIENCE 229(2024):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。