Formation of a Needle-Like Structure when Surface Flaking Occurs During the Rolling Contact Fatigue of a GCr15 Bearing
文献类型：期刊论文
| 作者 | Cheng Sheng1,2; Sun Yang1,3; Zhao Wenhui3; Luan Yikun1,2; Zheng Chengwu1,2; Li Dianzhong1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2024-04-11 |
| 卷号 | 60期号:4页码:425-433 |
| 关键词 | GCr15 bearing steel rolling contact fatigue surface crack needle-like structure |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2023.00005 |
| 通讯作者 | Zheng Chengwu(cwzheng@imr.ac) ; Li Dianzhong(dzli@imr.ac.cn) |
| 英文摘要 | As a form of damage caused by rolling contact, rolling contact fatigue (RCF) can lead to early pitting and flaking on the raceway surface of bearings, which is frequently accompanied by the propagation and fracture of RCF cracks. When the RCF crack is initiated on the raceway surface, large amount of stress, e. g., fluid pressurization, may be exerted close to the crack faces, which can not only accelerate the crack growth and cause rapid failure of the bearing but also lead to local microstructural alternations in the bearing steel. In this study, a needle-like structure was observed close to the cracks with flaking occurring during RCF in a GCr15 rolling bearing. The microstructures of the needle-like structure were analyzed via SEM, transmission Kikuchi diffraction (TKD), and TEM to elucidate its microstructural constitutions and characteristics. Results illustrated that the needle-like structure is a thin plate in three dimension decorated with some microvoids and equiaxed ferrite nanocrystalline formed at the interfaces. The formation of the needle-like structure was attributed to the local stress exerted close to the crack surface during the RCF of the bearings. This structure may be a type of decayed microstructure of the martensitic matrix of the bearing steel. With the increasing RCF stress cycles, the microvoids in the needle-like structure may facilitate the initiation and propagation of surface cracks preferentially, thus accelerating the occurrence of surface fatigue flaking in the bearing. |
| 资助项目 | National Natural Science Foundation of China[52031013] ; Strategic Priority Research Program of Chinese Academy of Sciences |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001208569500002 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Natural Science Foundation of China ; Strategic Priority Research Program of Chinese Academy of Sciences |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zheng Chengwu; Li Dianzhong |
| 作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Shenyang Univ Technol, Sch Mech Engn, Shenyang 110870, Peoples R China |
| 推荐引用方式 GB/T 7714 | Cheng Sheng,Sun Yang,Zhao Wenhui,et al. Formation of a Needle-Like Structure when Surface Flaking Occurs During the Rolling Contact Fatigue of a GCr15 Bearing[J]. ACTA METALLURGICA SINICA,2024,60(4):425-433. |
| APA | Cheng Sheng,Sun Yang,Zhao Wenhui,Luan Yikun,Zheng Chengwu,&Li Dianzhong.(2024).Formation of a Needle-Like Structure when Surface Flaking Occurs During the Rolling Contact Fatigue of a GCr15 Bearing.ACTA METALLURGICA SINICA,60(4),425-433. |
| MLA | Cheng Sheng,et al."Formation of a Needle-Like Structure when Surface Flaking Occurs During the Rolling Contact Fatigue of a GCr15 Bearing".ACTA METALLURGICA SINICA 60.4(2024):425-433. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。