Corrosion behavior of steel exposed to "zero" pollution atmosphere environment for 20 years
文献类型：期刊论文
| 作者 | Zhang, Simin1,2; Wang, Zhenyao2,3; Wang, Chuan2,3 |
| 刊名 | JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T
 |
| 出版日期 | 2024-05-01 |
| 卷号 | 30页码:2388-2396 |
| 关键词 | Atmospheric corrosion Q235 carbon steel 09CuPTiRE weathering steel X60 pipeline steel Clean atmosphere Corrosion behavior |
| ISSN号 | 2238-7854 |
| DOI | 10.1016/j.jmrt.2024.03.141 |
| 通讯作者 | Wang, Zhenyao(zhywang@imr.ac.cn) ; Wang, Chuan(cwang@imr.ac.cn) |
| 英文摘要 | In this study, the corrosion behavior of Q235 carbon steel, 09CuPTiRE weathering steel and X60 pipeline steel after 20 years exposure in "zero" pollution atmosphere environment was investigated by corrosion rate analysis, macroscopic observation, scanning electron microscopy, X-ray diffraction, white light interferometers and electrochemical analysis were conducted to analyze. The results showed that the corrosion rate of the three kinds of steels increases first and then decreases with time, and the results indicated that the empirical formula D = Atn was suitable for corrosion kinetics of three materials, and the three kinds of steels all form a relatively dense rust layer, which can effectively protect the metal matrix, inhibit the corrosion process and reduce the rate of corrosion. Under the same exposure time and the same corrosion conditions, the corrosion degree of the three materials is: X60 pipeline steel > Q235 Carbon steel >09CuPTiRE Weathering steel, three kinds of steel corrosion products are the same, only alpha-FeOOH and gamma-FeOOH exist in the rust layer, and the relative content of alpha-FeOOH is more than gamma-FeOOH of each steel in both skyward side and fieldward sides. X60 Pipeline steel has the worst corrosion resistance, and 09CuPTiRE weathering steel has the best corrosion resistance, so 09CuPTiRE weathering steel has better adaptability to this environment. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001225779500001 |
| 出版者 | ELSEVIER |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Zhenyao; Wang, Chuan |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 3.Natl Observat & Res Stn, Liaoning Shenyang Soil & Atmosphere Corros Mat, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Simin,Wang, Zhenyao,Wang, Chuan. Corrosion behavior of steel exposed to "zero" pollution atmosphere environment for 20 years[J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T,2024,30:2388-2396. |
| APA | Zhang, Simin,Wang, Zhenyao,&Wang, Chuan.(2024).Corrosion behavior of steel exposed to "zero" pollution atmosphere environment for 20 years.JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T,30,2388-2396. |
| MLA | Zhang, Simin,et al."Corrosion behavior of steel exposed to "zero" pollution atmosphere environment for 20 years".JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T 30(2024):2388-2396. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。