Corrosion mechanism of potassium silicate coating on Ti-6Al-4V alloys under solid NaCl deposit at 700 °C
文献类型：期刊论文
| 作者 | Chen, Zheng1,2; Du, Yao1,2; Lu, Yiliang2,3,5; Wang, Cheng2; Xin, Li2,4; Zhu, Shenglong2,4; Wang, Fuhui4 |
| 刊名 | CERAMICS INTERNATIONAL
 |
| 出版日期 | 2024-07-01 |
| 卷号 | 50期号:13页码:24594-24607 |
| 关键词 | Ti6Al4V alloys Potassium silicate coating NaCl High temperature corrosion |
| ISSN号 | 0272-8842 |
| DOI | 10.1016/j.ceramint.2024.04.194 |
| 通讯作者 | Zhu, Shenglong(slzhu@imr.ac.cn) |
| 英文摘要 | A potassium silicate coating cured by calcium hydrogen phosphate was prepared on Ti-6Al-4V, and its protection behavior against NaCl-induced corrosion was investigated at 700 degrees C for 500 h by the means of thermogravimetry, SEM, EMPA, XRD and TEM. The bare Ti-6Al-4V alloy suffered severe corrosion as the thickness of corrosion production layer exceeded 2 mm after 500 h. The major corrosion production was TiO2, and sodium titanates was observed within 100 h while disappeared after long-term tests. Accordingly, a novel model for NaCl-induced corrosion of Ti alloys at high temperatures was proposed. That is, the porosity of the corrosion product is strongly correlated with the reaction between water vapor in air and sodium titanates at high temperatures. The coating exhibited excellent protection as the corroded substrate layer, which is Ti5Si3 resulted from coating-substrate reaction, is similar to 6.6 mu m only, and no oxide scale was formed. Dissolution of Na in the coating was identified and is believed to be associated with the protective mechanism of the potassium silicate coating, i.e. this dissolution avoids chlorination-oxidation of Ti alloy. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:001243029100001 |
| 出版者 | ELSEVIER SCI LTD |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhu, Shenglong |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 3.Jiangsu JITRI Rd Engn Technol & Equipment Res Inst, Xuzhou 220005, Peoples R China 4.Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 5.State Grid Smart Grid Res Inst Co Ltd, State Key Lab Adv Power Transmiss Technol, Beijing 102209, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, Zheng,Du, Yao,Lu, Yiliang,et al. Corrosion mechanism of potassium silicate coating on Ti-6Al-4V alloys under solid NaCl deposit at 700 °C[J]. CERAMICS INTERNATIONAL,2024,50(13):24594-24607. |
| APA | Chen, Zheng.,Du, Yao.,Lu, Yiliang.,Wang, Cheng.,Xin, Li.,...&Wang, Fuhui.(2024).Corrosion mechanism of potassium silicate coating on Ti-6Al-4V alloys under solid NaCl deposit at 700 °C.CERAMICS INTERNATIONAL,50(13),24594-24607. |
| MLA | Chen, Zheng,et al."Corrosion mechanism of potassium silicate coating on Ti-6Al-4V alloys under solid NaCl deposit at 700 °C".CERAMICS INTERNATIONAL 50.13(2024):24594-24607. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。