Effect of heat treatment on the tribocorrosion behavior of 20Cr13 martensitic stainless steel
文献类型：期刊论文
| 作者 | Zhou, Yining1,2; Zhao, Zhichao3; Jiang, Shengli1,2; Duan, Deli2,3 |
| 刊名 | TRIBOLOGY INTERNATIONAL
 |
| 出版日期 | 2024-09-01 |
| 卷号 | 197页码:17 |
| 关键词 | 20Cr13 Microstructure Tribocorrosion Load NaCl solution |
| ISSN号 | 0301-679X |
| DOI | 10.1016/j.triboint.2024.109768 |
| 通讯作者 | Jiang, Shengli(sljiang@imr.ac.cn) ; Duan, Deli(duandl@imr.ac.cn) |
| 英文摘要 | In this study, we investigated the tribocorrosion behavior of 20Cr13 martensitic stainless steel subjected to different heat treatments. After quenching at 1000 degrees C, the steel was annealed and then tempered at 250 degrees C and 650 degrees C, resulting in two unique microstructures. These conditions, along with the annealed state, were examined for their tribocorrosion performance in a 3.5% NaCl solution. This study focused on the effects of applied load and microstructural changes on tribocorrosion characteristics. Experimental findings revealed that the opencircuit potential of the samples decreased with increasing load, while the corrosion current density increased. This indicated that corrosion influences wear in different ways: it accelerates wear by attacking the sample surface, and the formation of a tribocorrosion layer acts as a lubricant, reducing wear, especially under high loads. Among the tested conditions, the steel tempered at the lower temperature exhibited superior corrosion resistance and deformation resistance but showed less effective tribocorrosion resistance under low load conditions. This paper presents a quantitative analysis of material loss attributed to various factors, offering insights into the complex interactions at play in tribocorrosion processes. |
| WOS研究方向 | Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001242505300001 |
| 出版者 | ELSEVIER SCI LTD |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Jiang, Shengli; Duan, Deli |
| 作者单位 | 1.Chinese Acad Sci, CAS Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 3.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhou, Yining,Zhao, Zhichao,Jiang, Shengli,et al. Effect of heat treatment on the tribocorrosion behavior of 20Cr13 martensitic stainless steel[J]. TRIBOLOGY INTERNATIONAL,2024,197:17. |
| APA | Zhou, Yining,Zhao, Zhichao,Jiang, Shengli,&Duan, Deli.(2024).Effect of heat treatment on the tribocorrosion behavior of 20Cr13 martensitic stainless steel.TRIBOLOGY INTERNATIONAL,197,17. |
| MLA | Zhou, Yining,et al."Effect of heat treatment on the tribocorrosion behavior of 20Cr13 martensitic stainless steel".TRIBOLOGY INTERNATIONAL 197(2024):17. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。