Effect of the countersunk rivet head dimensions on fatigue behavior of riveted specimens of 2024-T3 alloy
文献类型：期刊论文
| 作者 | Lv, Guocheng1; Jia, Dawei2; Li, Changyou1; Zhao, Chunyu1; Zhang, Xiulu1; Yan, Feng3; Zhang, Hongzhuang1; Li, Bing1 |
| 刊名 | AIRCRAFT ENGINEERING AND AEROSPACE TECHNOLOGY
 |
| 出版日期 | 2024-08-27 |
| 页码 | 11 |
| 关键词 | Countersunk rivet Rivet head dimensions Fatigue behavior Riveted specimens 2024-T3 alloy |
| ISSN号 | 1748-8842 |
| DOI | 10.1108/AEAT-02-2024-0051 |
| 通讯作者 | Li, Changyou(chyli@mail.neu.edu.cn) |
| 英文摘要 | PurposeThis study aims to investigate the effect of countersunk rivet head dimensions on the fatigue performance of the riveted specimens of 2024-T3 alloy.Design/methodology/approachThe relationship between rivet head dimensions and fatigue behavior was investigated by finite element method and fatigue test. The fatigue fracture of the specimens was analyzed by scanning electron microscopy.FindingsA change of the rivet head dimensions will cause a change in the stress concentration and residual normal stress, the stress concentration near the rivet hole causes the fatigue crack source to be located on the straight section of the countersunk rivet hole and the residual normal stress can effectively restrain the initiation and expansion of fatigue cracks. The fatigue cycle will cause the rivet holes to produce different degrees of surface wear.Originality/valueThe fatigue life of the specimens with the height of the rivet head of 2.28 mm and 2.00 mm are similar, but the specimens with the height of the rivet head of 1.72 mm were far higher than the other specimens. |
| 资助项目 | National Natural Science Foundation of China[12272090] ; Opening fund of State Key Laboratory of Nonlinear Mechanics |
| WOS研究方向 | Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001297353400001 |
| 出版者 | EMERALD GROUP PUBLISHING LTD |
| 资助机构 | National Natural Science Foundation of China ; Opening fund of State Key Laboratory of Nonlinear Mechanics |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Li, Changyou |
| 作者单位 | 1.Northeastern Univ, Sch Mech Engn & Automat, Shenyang, Peoples R China 2.AVIC Shenyang Aircraft Corp, Shenyang, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lv, Guocheng,Jia, Dawei,Li, Changyou,et al. Effect of the countersunk rivet head dimensions on fatigue behavior of riveted specimens of 2024-T3 alloy[J]. AIRCRAFT ENGINEERING AND AEROSPACE TECHNOLOGY,2024:11. |
| APA | Lv, Guocheng.,Jia, Dawei.,Li, Changyou.,Zhao, Chunyu.,Zhang, Xiulu.,...&Li, Bing.(2024).Effect of the countersunk rivet head dimensions on fatigue behavior of riveted specimens of 2024-T3 alloy.AIRCRAFT ENGINEERING AND AEROSPACE TECHNOLOGY,11. |
| MLA | Lv, Guocheng,et al."Effect of the countersunk rivet head dimensions on fatigue behavior of riveted specimens of 2024-T3 alloy".AIRCRAFT ENGINEERING AND AEROSPACE TECHNOLOGY (2024):11. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。