Effect of heat treatment on microstructure, mechanical properties and corrosion behavior of LACSed 7075 deposits
文献类型：期刊论文
| 作者 | Wang, Kang1,2; Cui, Xinyu1; Wang, Jiqiang1; Xiong, Tianying1 |
| 刊名 | MATERIALS CHARACTERIZATION
 |
| 出版日期 | 2024-11-01 |
| 卷号 | 217页码:13 |
| 关键词 | Laser-assisted cold spray Heat treatment Mechanical properties Corrosion behavior |
| ISSN号 | 1044-5803 |
| DOI | 10.1016/j.matchar.2024.114424 |
| 通讯作者 | Wang, Jiqiang(jqwang11s@imr.ac.cn) |
| 英文摘要 | Laser-assisted cold spray presents advantages in the additive manufacturing of high-strength 7075 aluminum alloy. In this paper, four heat treatment methods, including T6, T73, RRA, and annealing, were employed to further improve the mechanical properties and corrosion resistance of LACSed 7075 deposits. The relationship between their microstructures and performances was systematically investigated as well. SEM, EBSD, XRD, and TEM were used to observe the microstructure evolution of deposits after heat treatments in detail. Tensile test, IGC test, and potentiodynamic polarization curve test were performed to evaluate their mechanical and corrosion performances. The results showed that the grain structure maintained its anisotropy despite abnormal grain growth and static recrystallization following the heat treatments. The matrix precipitates and grain boundary precipitates showed distinct morphologies (size and shape) after different heat treatments, which had major impacts on the deposits' performances. The test results revealed that the T6 and RRA samples achieved highest yield strength of approximately 470 MPa. The elongation ratio of the LACSed deposits was greatly improved after annealing. The T73 and RRA samples exhibited much better corrosion resistance than the other samples. The evidence verified that typical post-heat treatments are feasible for improving the performance of LACSed 7075 deposits. |
| 资助项目 | Youth Innovation Pro-motion Association[2023199] ; Chinese Academy of Sciences (CAS) |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001336235600001 |
| 出版者 | ELSEVIER SCIENCE INC |
| 资助机构 | Youth Innovation Pro-motion Association ; Chinese Academy of Sciences (CAS) |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Jiqiang |
| 作者单位 | 1.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Kang,Cui, Xinyu,Wang, Jiqiang,et al. Effect of heat treatment on microstructure, mechanical properties and corrosion behavior of LACSed 7075 deposits[J]. MATERIALS CHARACTERIZATION,2024,217:13. |
| APA | Wang, Kang,Cui, Xinyu,Wang, Jiqiang,&Xiong, Tianying.(2024).Effect of heat treatment on microstructure, mechanical properties and corrosion behavior of LACSed 7075 deposits.MATERIALS CHARACTERIZATION,217,13. |
| MLA | Wang, Kang,et al."Effect of heat treatment on microstructure, mechanical properties and corrosion behavior of LACSed 7075 deposits".MATERIALS CHARACTERIZATION 217(2024):13. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。