Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures
文献类型：期刊论文
| 作者 | Wang, Huyue1,2; Ming, Hongliang2; Wang, Jianqiu2,3; Han, En-Hou2,3 |
| 刊名 | JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
 |
| 出版日期 | 2024-11-18 |
| 页码 | 10 |
| 关键词 | failure analysis fractography gaseous hydrogen hydrogen embrittlement mechanical testing X42 pipeline steel |
| ISSN号 | 1059-9495 |
| DOI | 10.1007/s11665-024-10457-y |
| 通讯作者 | Ming, Hongliang(hlming12s@imr.ac.cn) ; Wang, Jianqiu(wangjianqiu@imr.ac.cn) |
| 英文摘要 | This work explored the effect of pressure on the hydrogen embrittlement behavior of X42 pipeline steel by using tensile test. Fracture mode changes from ductile fracture when exposed to nitrogen to coexistence of ductile and brittle fracture in the presence of hydrogen. Furthermore, it has been observed that raising the hydrogen pressure can significantly increase the susceptibility to hydrogen embrittlement. This is supported by the presence of a greater proportion of brittle characteristic area on the cross section at fracture. The hydrogen embrittlement susceptibility index reaches 13.05% at pressure of 4 MPa, approximately 1.7 times higher than that at the pressure of 2 MPa. |
| 资助项目 | National Key R&D Program of China[2021YFB4001601] ; Youth Innovation Promotion Association CAS[2022187] |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:001357758000001 |
| 出版者 | SPRINGER |
| 资助机构 | National Key R&D Program of China ; Youth Innovation Promotion Association CAS |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ming, Hongliang; Wang, Jianqiu |
| 作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 2.Chinese Acad Sci, CAS Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Peoples R China 3.Inst Corros Sci & Technol, Guangzhou 510530, Guangdong, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Huyue,Ming, Hongliang,Wang, Jianqiu,et al. Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2024:10. |
| APA | Wang, Huyue,Ming, Hongliang,Wang, Jianqiu,&Han, En-Hou.(2024).Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,10. |
| MLA | Wang, Huyue,et al."Hydrogen Embrittlement Behavior of X42 Pipeline Steel in Gaseous Hydrogen with Different Pressures".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE (2024):10. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。