Effects of Cu Content on the Microstructure and Tensile Property of K4061 Alloy
文献类型：期刊论文
| 作者 | Cao, Shuting1,2; Zhao, Jian3; Gong, Tongzhao1; Zhang, Shaohua1; Zhang, Jian1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2024-09-11 |
| 卷号 | 60期号:9页码:1179-1188 |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2022.00427 |
| 通讯作者 | Zhang, Shaohua(zhangshaohua@imr.ac.cn) |
| 英文摘要 | Al-Cu alloy has broad application prospects in the field of aerospace due to its excellent performance. In this paper, deposits with different Cu contents were prepared by the wire arc additive manufacturing (WAAM) process, and the effects of Cu content on the microstructure and mechanical properties were investigated. The microstructure of Al-Cu alloy was investigated by metallography, scanning electron microscope (SEM), energy-dispersive spectrometer (EDS), and transmission electron microscope (TEM). The results show that both the number and size of the precipitated theta phases (Al2Cu) in the as-deposited material increase with the increase of Cu content. After the T4 treatment, the solid solution amount of Cu in the matrix showed a trend of first increasing and then remaining stable. When the content of Cu was greater than 5.65%, as the Cu content increased, the number and size of the remaining theta phases both increased. In the peak ageing state, the amount of precipitated theta' phase showed a trend of increasing and then remaining stable. After the T6 treatment, the mechanical properties showed a trend of first increasing and then decreasing with the increase of the content of Cu. When the Cu content was 5.65%, the deposit achieved the best mechanical properties, and the anisotropy of the mechanical properties disappeared. The tensile strength, yield strength, and elongation reached 538 MPa, 478 MPa, and 10.5%, respectively. When the content of Cu was greater than 5.65%, the anisotropy of mechanical properties was obvious, and the fracture mode of the vertical specimen changed from ductile fracture to brittle fracture. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:001320333900003 |
| 出版者 | SCIENCE PRESS |
| 源URL |  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, Shaohua |
| 作者单位 | 1.Chinese Acad Sci, Shi Changxu Innovat Ctr Adv Mat, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Xian Aerosp Prop Inst, Xian 710100, Peoples R China |
| 推荐引用方式 GB/T 7714 | Cao, Shuting,Zhao, Jian,Gong, Tongzhao,et al. Effects of Cu Content on the Microstructure and Tensile Property of K4061 Alloy[J]. ACTA METALLURGICA SINICA,2024,60(9):1179-1188. |
| APA | Cao, Shuting,Zhao, Jian,Gong, Tongzhao,Zhang, Shaohua,&Zhang, Jian.(2024).Effects of Cu Content on the Microstructure and Tensile Property of K4061 Alloy.ACTA METALLURGICA SINICA,60(9),1179-1188. |
| MLA | Cao, Shuting,et al."Effects of Cu Content on the Microstructure and Tensile Property of K4061 Alloy".ACTA METALLURGICA SINICA 60.9(2024):1179-1188. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。