Preparation of core-shell type particles by injection method
文献类型:会议论文
作者 | Chen, Y. F.; Chen, Y. F.; Chen, Y. F. |
出版日期 | 2003 |
会议名称 | 7th International Symposium on Functionally Grade Materials (FGM2002) |
会议日期 | OCT 15-18, 2002 |
会议地点 | BEIJING, PEOPLES R CHINA |
关键词 | core-shell type particles monodisperse silica Al(OH)(3) coating layer injection method silicon-nitride alumina hydrate coated powders composites layers |
页码 | 143-146 |
中文摘要 | SiO2@ Al(OH)(3) core-shell type particles were prepared by injecting Al(NO3)(3) solution into NaHCO3 solution in which the SiO2 core particles were dispersed. The monodisperse SiO2 core particles with a diameter of around 300 nm were prepared by a seeding technique on the basis of hydrolyzing tetraethylorthosilicate (TEOS) in aqueous ethanol solutions with ammonia as catalyst. The shell with a thickness of 33 nm could be deposited on SiO2 spheres without free Al(OH)(3) particles observable under proper experimental conditions such as 0.5M NaHCO3, 20g/L SiO2, 0.15 M Al(NO3)(3) and 0.1 ml/min as injection speed. |
收录类别 | CPCI |
会议网址 | |
会议录 | FUNCTIONALLY GRADED MATERIALS VII 丛书: MATERIALS SCIENCE FORUM |
会议录出版者 | Trans Tech Publications Ltd |
语种 | 英语 |
源URL | [http://ir.ipe.ac.cn/handle/122111/5333] |
专题 | 过程工程研究所_多相复杂系统国家重点实验室 |
推荐引用方式 GB/T 7714 |
Chen, Y. F.,Chen, Y. F.,Chen, Y. F.. Preparation of core-shell type particles by injection method[C]. 见:7th International Symposium on Functionally Grade Materials (FGM2002). BEIJING, PEOPLES R CHINA. OCT 15-18, 2002. |
入库方式: OAI收割
来源:过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。