Ce-doped YAG phosphor powders prepared by co-precipitation and heterogeneous precipitation
文献类型:期刊论文
作者 | Yuan, FL; Ryu, HJ |
刊名 | MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY
![]() |
出版日期 | 2004-02-25 |
卷号 | 107期号:1页码:14-18 |
关键词 | YAG co-precipitation heterogeneous precipitation Ce-doping powders |
ISSN号 | 0921-5107 |
其他题名 | Mater. Sci. Eng. B-Solid State Mater. Adv. Technol. |
中文摘要 | Ce-doped YAG phosphor powders were prepared by co-precipitation and heterogeneous precipitation methods using ammonium hydrogen carbonate as precipitant. Pure Ce-doped YAG phase was obtained by calcining the precipitate at 1200degreesC. The emission intensity of Ce-doped YAG phosphor was found to increase with increases in the calcining temperature, and there was a clear shift of peaks to longer wavelengths. The emission intensity of two samples was compared. It was found that, calcining below 1340degreesC, the emission intensity of sample prepared by co-precipitation was higher, on the other hand, calcining above 1340degreesC, the emission intensity of sample prepared by heterogeneous precipitation was higher. (C) 2003 Elsevier B.V. All rights reserved. |
英文摘要 | Ce-doped YAG phosphor powders were prepared by co-precipitation and heterogeneous precipitation methods using ammonium hydrogen carbonate as precipitant. Pure Ce-doped YAG phase was obtained by calcining the precipitate at 1200degreesC. The emission intensity of Ce-doped YAG phosphor was found to increase with increases in the calcining temperature, and there was a clear shift of peaks to longer wavelengths. The emission intensity of two samples was compared. It was found that, calcining below 1340degreesC, the emission intensity of sample prepared by co-precipitation was higher, on the other hand, calcining above 1340degreesC, the emission intensity of sample prepared by heterogeneous precipitation was higher. (C) 2003 Elsevier B.V. All rights reserved. |
WOS标题词 | Science & Technology ; Technology ; Physical Sciences |
类目[WOS] | Materials Science, Multidisciplinary ; Physics, Condensed Matter |
研究领域[WOS] | Materials Science ; Physics |
关键词[WOS] | YTTRIUM-ALUMINUM-GARNET ; COMBUSTION PROCESS ; SPRAY-PYROLYSIS ; LUMINESCENCE |
收录类别 | SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000220291100003 |
公开日期 | 2013-11-05 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/4904] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | 1.Korea Res Inst Chem Technol, Adv Mat Div, Taejon 305600, South Korea 2.Chinese Acad Sci, Inst Proc Engn, Beijing 100080, Peoples R China |
推荐引用方式 GB/T 7714 | Yuan, FL,Ryu, HJ. Ce-doped YAG phosphor powders prepared by co-precipitation and heterogeneous precipitation[J]. MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY,2004,107(1):14-18. |
APA | Yuan, FL,&Ryu, HJ.(2004).Ce-doped YAG phosphor powders prepared by co-precipitation and heterogeneous precipitation.MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY,107(1),14-18. |
MLA | Yuan, FL,et al."Ce-doped YAG phosphor powders prepared by co-precipitation and heterogeneous precipitation".MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY 107.1(2004):14-18. |
入库方式: OAI收割
来源:过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。