Activation energy for conduction in Y2O3-stabilized zirconia
文献类型:期刊论文
作者 | Li, Y; Gong, JH; Xie, YS; Tang, ZL; Chen, YF; Zhang, ZT |
刊名 | JOURNAL OF INORGANIC MATERIALS
![]() |
出版日期 | 2002-07-01 |
卷号 | 17期号:4页码:811-816 |
关键词 | ionic conductivity activation energy for conduction defect association ZrO2-based solid electrolytes |
ISSN号 | 1000-324X |
其他题名 | J. Inorg. Mater. |
中文摘要 | The ac conductivity spectra were measured in the temperature range from 313 to 473K for a Y2O3-stabilized ZrO2 (YSZ). Then the dc conductivity was deduced and its temperature dependence analyzed. It was shown that, at low temperatures, the activation energy for conduction in YSZ increases with increasing temperature. This experimental phenomenon is rather different with those observed previously in the high temperature range in which the activation energy was found to decrease with increasing temperature. Based on the analyses of the mechanisms for disassociation and migration of oxygen vacancies in the materials, a reasonable explanation for the temperature dependence of the activation energy for conduction in YSZ was proposed. |
英文摘要 | The ac conductivity spectra were measured in the temperature range from 313 to 473K for a Y2O3-stabilized ZrO2 (YSZ). Then the dc conductivity was deduced and its temperature dependence analyzed. It was shown that, at low temperatures, the activation energy for conduction in YSZ increases with increasing temperature. This experimental phenomenon is rather different with those observed previously in the high temperature range in which the activation energy was found to decrease with increasing temperature. Based on the analyses of the mechanisms for disassociation and migration of oxygen vacancies in the materials, a reasonable explanation for the temperature dependence of the activation energy for conduction in YSZ was proposed. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Ceramics |
研究领域[WOS] | Materials Science |
关键词[WOS] | YTTRIA-STABILIZED ZIRCONIA ; TEMPERATURE IONIC-CONDUCTIVITY ; SINGLE-CRYSTALS ; AC CONDUCTIVITY |
收录类别 | SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000177309800028 |
公开日期 | 2013-11-12 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/5621] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | 1.Chinese Acad Sci, Inst Chem Met, Beijing 100080, Peoples R China 2.Tsing Hua Univ, Dept Mat Sci & Engn, Beijing 100084, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Y,Gong, JH,Xie, YS,et al. Activation energy for conduction in Y2O3-stabilized zirconia[J]. JOURNAL OF INORGANIC MATERIALS,2002,17(4):811-816. |
APA | Li, Y,Gong, JH,Xie, YS,Tang, ZL,Chen, YF,&Zhang, ZT.(2002).Activation energy for conduction in Y2O3-stabilized zirconia.JOURNAL OF INORGANIC MATERIALS,17(4),811-816. |
MLA | Li, Y,et al."Activation energy for conduction in Y2O3-stabilized zirconia".JOURNAL OF INORGANIC MATERIALS 17.4(2002):811-816. |
入库方式: OAI收割
来源:过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。