Kinetics of reduction of iron oxide in CaO-SiO2-Al2O3-FetO slags with graphite powder
文献类型：期刊论文
| 作者 | Yang, XM; Huang, DB; Kong, LT; Yang, TJ; Xie, YS; Wang, DG |
| 刊名 | JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
 |
| 出版日期 | 1998-04-01 |
| 卷号 | 5期号:1页码:21-27 |
| 关键词 | CaO-SiO2-Al2O3-FetO slags reduction rate graphite powder FetO activity kinetics |
| ISSN号 | 1006-706X |
| 其他题名 | J. Iron Steel Res. Int. |
| 中文摘要 | The reduction rate of FetO in CaO-SiO2-Al2O3-FetO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and FetO content on the reduction rare have also been discussed Test results show that the reduction rate increases with the increase of temperature or FetO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. Thr maximum reduction rate is observed around CaO/SiO2 = 1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to FetO content or FetO activity calculated by using regular solution model. The reduction rate of FetO in CaO-SiO2-Al2O3-FetO slags with graphite powder is in the range of 0.15 X 10(-4)-0.86 X 10(-4) mol-O/cm(2).s. |
| 英文摘要 | The reduction rate of FetO in CaO-SiO2-Al2O3-FetO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and FetO content on the reduction rare have also been discussed Test results show that the reduction rate increases with the increase of temperature or FetO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. Thr maximum reduction rate is observed around CaO/SiO2 = 1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to FetO content or FetO activity calculated by using regular solution model. The reduction rate of FetO in CaO-SiO2-Al2O3-FetO slags with graphite powder is in the range of 0.15 X 10(-4)-0.86 X 10(-4) mol-O/cm(2).s. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Metallurgy & Metallurgical Engineering |
| 研究领域[WOS] | Metallurgy & Metallurgical Engineering |
| 关键词[WOS] | OPTICAL BASICITY ; MATHEMATICAL EXPRESSION ; QUADRATIC FORMALISM ; STEELMAKING PROCESS ; PHOSPHORUS |
| 收录类别 | SCI |
| 原文出处 | |
| 语种 | 英语 |
| WOS记录号 | WOS:000075558100005 |
| 公开日期 | 2013-11-15 |
| 版本 | 出版稿 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/5979]  |
| 专题 | 过程工程研究所_研究所（批量导入） |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem Met, Beijing 100080, Peoples R China 2.Beijing Univ Sci & Technol, Beijing 100083, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, XM,Huang, DB,Kong, LT,et al. Kinetics of reduction of iron oxide in CaO-SiO2-Al2O3-FetO slags with graphite powder[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,1998,5(1):21-27. |
| APA | Yang, XM,Huang, DB,Kong, LT,Yang, TJ,Xie, YS,&Wang, DG.(1998).Kinetics of reduction of iron oxide in CaO-SiO2-Al2O3-FetO slags with graphite powder.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,5(1),21-27. |
| MLA | Yang, XM,et al."Kinetics of reduction of iron oxide in CaO-SiO2-Al2O3-FetO slags with graphite powder".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 5.1(1998):21-27. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。