Preparation of silica-based inorganic-organic hybrid membrane via the sol-gel route
文献类型:期刊论文
作者 | Zhang, GC; Chen, YF![]() |
刊名 | JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
![]() |
出版日期 | 2000-12-01 |
卷号 | 19期号:1-3页码:425-428 |
关键词 | sol-gel inorganic-organic hybrid membrane permeation characterization |
ISSN号 | 0928-0707 |
其他题名 | J. Sol-Gel Sci. Technol. |
中文摘要 | Silica-based inorganic-organic hybrid membranes have been prepared on porous alpha -Al2O3 substrate (pore size, 2 mum) using tetraethoxysilane (TEOS) and phenyltrimethoxysilane (PTMOS) as precursors. The effects of sol synthesis conditions on the processing and performance of deposited hybrid layers were observed. The thickness of the hybrid layers after three deposition cycles is about 2 mum, estimated from their cross-section SEM micrographs. The gas permselectivity of the hybrid membrane was characterized by O-2/N-2, CO2/N-2, and CO2/O-2 mixing gases, which was mainly governed by the surface diffusion at lower pressures and Knudson diffusion at higher pressures. The introduction of phenyl groups can not only improve the selectivity of O-2/N-2 and CO2/N-2, but also densify the membrane network. |
英文摘要 | Silica-based inorganic-organic hybrid membranes have been prepared on porous alpha -Al2O3 substrate (pore size, 2 mum) using tetraethoxysilane (TEOS) and phenyltrimethoxysilane (PTMOS) as precursors. The effects of sol synthesis conditions on the processing and performance of deposited hybrid layers were observed. The thickness of the hybrid layers after three deposition cycles is about 2 mum, estimated from their cross-section SEM micrographs. The gas permselectivity of the hybrid membrane was characterized by O-2/N-2, CO2/N-2, and CO2/O-2 mixing gases, which was mainly governed by the surface diffusion at lower pressures and Knudson diffusion at higher pressures. The introduction of phenyl groups can not only improve the selectivity of O-2/N-2 and CO2/N-2, but also densify the membrane network. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Ceramics |
研究领域[WOS] | Materials Science |
收录类别 | ISTP ; SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000166544900079 |
公开日期 | 2013-11-15 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/6030] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | Chinese Acad Sci, Inst Chem Met, Beijing 100080, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, GC,Chen, YF,Li, HY,et al. Preparation of silica-based inorganic-organic hybrid membrane via the sol-gel route[J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,2000,19(1-3):425-428. |
APA | Zhang, GC,Chen, YF,Li, HY,&Xie, YS.(2000).Preparation of silica-based inorganic-organic hybrid membrane via the sol-gel route.JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,19(1-3),425-428. |
MLA | Zhang, GC,et al."Preparation of silica-based inorganic-organic hybrid membrane via the sol-gel route".JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY 19.1-3(2000):425-428. |
入库方式: OAI收割
来源:过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。