纳米MoS2空间润滑脂的真空高温摩擦学特性研究
文献类型：会议论文
| 作者 | 孙晓军
|
| 出版日期 | 2013 |
| 会议名称 | 第十七届全国润滑脂技术交流会 |
| 会议日期 | 2013-10-10~2013-10-14 |
| 会议地点 | 广西桂林 |
| 关键词 | MoS2纳米片 空间润滑脂 摩擦磨损 MoS2 nano-slices Space lubricating grease Friction and wear |
| 页码 | 1-8 |
| 通讯作者 | 胡献国 |
| 中文摘要 | 分别利用微米MoS2和MoS2纳米片制备出聚α烯烃基合成空间润滑脂，利用空间摩擦磨损试验机考察了两种形态的MoS2对空间润滑脂的真空高温摩擦学性能的影响。利用原子力显微镜考察了磨损表面的形貌，并采用X射线光电子能谱仪(XPS)表征了磨损后的表面元素与价态，探讨了其摩擦磨损机理。结果表明：在真空高温条件下，MoS2纳米片比微米MoS2更能改善空间润滑脂的摩擦学性能。MoS2纳米片可以在摩擦表面发生摩擦化学反应，形成润滑保护膜，降低摩擦磨损。 |
| 英文摘要 | The tribological properties of PAO-based space lubricating grease containing MoS2 with different sizes and morphologies were evaluated using a Space-tribometer. The morphologies of the worn surfaces were observed by Atomic Force Microscope. Both elements and valence states on the worn surface were analyzed using X-ray photoelectron spectrometer. The results showed that nano-ball MoS2 was not suitable to act as antiwear and antifriction additive in PAO-based space grease. The nano-slices MoS2 was better than micro-MoS2 in space-tribological properties under vacuum and high temperature. The nano- slices MoS2 took place tribo-chemical reaction on the rubbing surface and formed lubricating film, and then reduced the wear. |
| 语种 | 中文 |
| 源URL | [http://210.77.64.217/handle/362003/4557]  |
| 专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
| 推荐引用方式 GB/T 7714 | 孙晓军. 纳米MoS2空间润滑脂的真空高温摩擦学特性研究[C]. 见:第十七届全国润滑脂技术交流会. 广西桂林. 2013-10-10~2013-10-14. |
入库方式： OAI收割
来源：兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。