Fabrication of superhydrophobic surfaces on aluminum
文献类型：期刊论文
| 作者 | Wang H ; Dai D ; Wu XD |
| 刊名 | Applied Surface Science
 |
| 出版日期 | 2008 |
| 期号 | 254页码:5599–5601 |
| 关键词 | Superhydrophobic surface Anodization Aluminum Low-temperature plasma treatment |
| 合作状况 | 国内 |
| 中文摘要 | A superhydrophobic surface was prepared on aluminum substrate. Anodization and low-temperature plasma treatment were used to create micro-nano-structure and subsequently trichlorooctadecyl-silane modified the rough surface. The result shows that the water static contact of the aluminum surface after anodization and modification by trichlorooctadecyl-silane reaches to 152.1°. A rougher surface with some micro-nano-pores and small mastoids along the edges of pores was generated when low-temperature plasma treatment was applied to anodized aluminum film, resulting in water static contact angle up to 157.8°. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2009-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/120]  |
| 专题 | 宁波材料技术与工程研究所_宁波所知识产出 |
| 推荐引用方式 GB/T 7714 | Wang H,Dai D,Wu XD. Fabrication of superhydrophobic surfaces on aluminum[J]. Applied Surface Science,2008(254):5599–5601. |
| APA | Wang H,Dai D,&Wu XD.(2008).Fabrication of superhydrophobic surfaces on aluminum.Applied Surface Science(254),5599–5601. |
| MLA | Wang H,et al."Fabrication of superhydrophobic surfaces on aluminum".Applied Surface Science .254(2008):5599–5601. |