Fabrication of Cr coating on AZ31 magnesium alloy by magnetron sputtering
文献类型：期刊论文
| 作者 | Wu GS ; Wang AY ; Ding KJ ; Xu CY ; Dai W ; Xu AJ |
| 刊名 | Trans．Nonferrous Met．Soc．China
 |
| 出版日期 | 2008 |
| 期号 | 18页码:s329-s333 |
| 关键词 | magnesium alloy Cr coating magnetron sputtering corrosion |
| 合作状况 | 国内 |
| 中文摘要 | Chromium-plating is considered an effective method to improve surface propegies of meta1 materials．Magnetron sputtering was applied to prepare Cr coating on AZ3l magnesium alloy and the influence of bias voltage on properties of Cr coating was investigated．The obtained coatings present an (110) preferred texture and have a developed columnar structure．With increasing bias voltage, the surface structure of Cr coating becomes denser．Al1 of the Cr-coated AZ31 have much higher surface microhardness than bare AZ31．The Cr coating deposited on AZ31 at bias voltage of-150 V has a higher corrosion potential than others．The result of the immersion test shows that it decreases the damaged area compared with bare AZ31．The failure of the coated AZ3l is mainly attributed to the existence of through-thickness defects in the coating． |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2009-12-25 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/124]  |
| 专题 | 宁波材料技术与工程研究所_宁波所知识产出 |
| 推荐引用方式 GB/T 7714 | Wu GS,Wang AY,Ding KJ,et al. Fabrication of Cr coating on AZ31 magnesium alloy by magnetron sputtering[J]. Trans．Nonferrous Met．Soc．China,2008(18):s329-s333. |
| APA | Wu GS,Wang AY,Ding KJ,Xu CY,Dai W,&Xu AJ.(2008).Fabrication of Cr coating on AZ31 magnesium alloy by magnetron sputtering.Trans．Nonferrous Met．Soc．China(18),s329-s333. |
| MLA | Wu GS,et al."Fabrication of Cr coating on AZ31 magnesium alloy by magnetron sputtering".Trans．Nonferrous Met．Soc．China .18(2008):s329-s333. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0