Effect of chemical composition on grain boundary microchemistry and stress corrosion cracking in Alloy 182
文献类型：期刊论文
| 作者 | Q. J. Peng ; J. Hou ; Y. Takeda ; T. Shoji |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2013 |
| 卷号 | 67页码:91-99 |
| 关键词 | Superalloys AES Stress corrosion Welding high-temperature water ductility-dip cracking heat-affected zone boron segregation minor elements nickel-alloys nbc particles base alloys weld metal microstructure |
| ISSN号 | 0010-938X |
| 原文出处 | |
| 语种 | 英语 |
| 公开日期 | 2013-12-24 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/71425]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. J. Peng,J. Hou,Y. Takeda,et al. Effect of chemical composition on grain boundary microchemistry and stress corrosion cracking in Alloy 182[J]. Corrosion Science,2013,67:91-99. |
| APA | Q. J. Peng,J. Hou,Y. Takeda,&T. Shoji.(2013).Effect of chemical composition on grain boundary microchemistry and stress corrosion cracking in Alloy 182.Corrosion Science,67,91-99. |
| MLA | Q. J. Peng,et al."Effect of chemical composition on grain boundary microchemistry and stress corrosion cracking in Alloy 182".Corrosion Science 67(2013):91-99. |