A Cr2O3-deposited Sm(Co0.68Fe0.22Cu0.08Zr0.02)(7.5) magnet with increased oxidation resistance at 700 degrees C
文献类型：期刊论文
| 作者 | H. Zhao ; X. Peng ; Q. Feng ; Z. Guo ; W. Li ; F. Wang |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2013 |
| 卷号 | 73页码:245-249 |
| 关键词 | Alloy SEM TEM XRD Oxidation Oxide coatings high-temperature magnets permanent-magnets internal nitridation thermal-stability smco alloys nickel microstructure diffusion |
| ISSN号 | 0010-938X |
| 原文出处 | |
| 语种 | 英语 |
| 公开日期 | 2013-12-24 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/71708]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Zhao,X. Peng,Q. Feng,et al. A Cr2O3-deposited Sm(Co0.68Fe0.22Cu0.08Zr0.02)(7.5) magnet with increased oxidation resistance at 700 degrees C[J]. Corrosion Science,2013,73:245-249. |
| APA | H. Zhao,X. Peng,Q. Feng,Z. Guo,W. Li,&F. Wang.(2013).A Cr2O3-deposited Sm(Co0.68Fe0.22Cu0.08Zr0.02)(7.5) magnet with increased oxidation resistance at 700 degrees C.Corrosion Science,73,245-249. |
| MLA | H. Zhao,et al."A Cr2O3-deposited Sm(Co0.68Fe0.22Cu0.08Zr0.02)(7.5) magnet with increased oxidation resistance at 700 degrees C".Corrosion Science 73(2013):245-249. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。