Preparation and characterization of atmospheric plasma-sprayed NiCr/Cr3C2-BaF2 center dot CaF2 composite coating
文献类型：期刊论文
| 作者 | Huang, Chuanbing1,2; Du, Lingzhong1; Zhang, Weigang1 |
| 刊名 | SURFACE & COATINGS TECHNOLOGY
 |
| 出版日期 | 2009-07-15 |
| 卷号 | 203期号:20-21页码:3058-3065 |
| 关键词 | Plasma spray NiCr/Cr3C2-BaF2 center dot CaF2 Coated powders Solid lubricant Tribological properties Wear mechanism |
| ISSN号 | 0257-8972 |
| 通讯作者 | Huang, CB |
| 英文摘要 | NiCr alloy-coated BaF2 center dot CaF2 eutectic and Cr3C2 powders were respectively prepared by both pressurized hydrogen reduction and solid state alloying technology. Using this NiCr/Cr3C2-BaF2 center dot CaF2 composite powder, a derived coating was produced by atmospheric plasma spray (APS) technology. Microstructures and phase compositions of the powders, as well as the deposited coating, were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The friction and wear behavior of the coatings from ambient temperature to 800 degrees C was evaluated using a ball-on-disk tribometer. The results show that the NiCr/Cr3C2-BaF2 center dot CaF2 composite coating exhibited low porosity, high microhardness and high cohesive strength, which result in good friction reduction and excellent anti-wear ability at elevated temperatures up to 800 degrees C. The friction coefficient of NiCr/Cr3C2-BaF2 center dot CaF2 coating decreases with increasing temperature. The wear rates of both coating and couple balls are significantly lower at temperatures above 500 degrees C than those tested at room temperature. From the investigation of worn surfaces, it was concluded that brittle fracture and delamination were the dominant wear mechanisms of the coatings at low temperature. A transition stage from brittle to plastic state with decreased shear strength was observed for BaF2 center dot CaF2 eutectic at high temperatures, which resulted in the formation of a continuous lubricating layer in the wear track above 500 degrees C The excellent mechanical properties of the coating were partially attributed to the protection of NiCr layer of the composite powders which decreased the oxidation. decarburization and ablation of Cr3C2-BaF2 center dot CaF2 during spraying. (C) 2009 Elsevier B.V. All rights reserved. |
| WOS标题词 | Science & Technology ; Technology ; Physical Sciences |
| 类目[WOS] | Materials Science, Coatings & Films ; Physics, Applied |
| 研究领域[WOS] | Materials Science ; Physics |
| 关键词[WOS] | HIGH-TEMPERATURE ; WEAR BEHAVIOR ; TRIBOLOGICAL PROPERTIES ; CR3C2-NICR COATINGS ; SOLID LUBRICANTS ; FRICTION ; IMPROVEMENT ; OXIDATION ; SURFACE |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000267632400013 |
| 公开日期 | 2013-12-06 |
| 版本 | 出版稿 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/6635]  |
| 专题 | 过程工程研究所_多相复杂系统国家重点实验室 |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Huang, Chuanbing,Du, Lingzhong,Zhang, Weigang. Preparation and characterization of atmospheric plasma-sprayed NiCr/Cr3C2-BaF2 center dot CaF2 composite coating[J]. SURFACE & COATINGS TECHNOLOGY,2009,203(20-21):3058-3065. |
| APA | Huang, Chuanbing,Du, Lingzhong,&Zhang, Weigang.(2009).Preparation and characterization of atmospheric plasma-sprayed NiCr/Cr3C2-BaF2 center dot CaF2 composite coating.SURFACE & COATINGS TECHNOLOGY,203(20-21),3058-3065. |
| MLA | Huang, Chuanbing,et al."Preparation and characterization of atmospheric plasma-sprayed NiCr/Cr3C2-BaF2 center dot CaF2 composite coating".SURFACE & COATINGS TECHNOLOGY 203.20-21(2009):3058-3065. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。