A Feasible Post-Treatment of Drying and Rewetting for Preparation of High-Flux Pluronic F127/Polyethersulfone Nanofiltration Membranes
文献类型:期刊论文
作者 | Zhang, Yan1; Su, Yanlei1,2; Chen, Wenjuan1; Peng, Jinming1; Dong, Yanan1; Jiang, Zhongyi1 |
刊名 | INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH
![]() |
出版日期 | 2011-04-20 |
卷号 | 50期号:8页码:4678-4685 |
关键词 | solvent-resistant nanofiltration ultrafiltration membranes polyethersulfone membranes composite membranes molecular-level hollow fibers performance f127 spectroscopy |
ISSN号 | 0888-5885 |
其他题名 | Ind. Eng. Chem. Res. |
中文摘要 | Pluronic F127/polyethersulfone (PES) blend nanofiltration membranes were fabricated by varying polymer weight ratios Of W(F127)/W(PES) in casting solutions from 0.0 to 100.0 wt %. The initial wet membranes prepared via the phase inversion method were post treated by drying at room temperature and then immersion into water for rewetting to obtain Pluronic F127/PES nanofiltration membranes. Membrane shrinkage and swelling, cross section and surface morphologies, water uptake, surface hydrophilicity, X-ray diffraction pattern, water flux, and rejection of dyes for Pluronic F127/PES nanofiltration membranes were investigated The introduction of pluronic F127 into PES membranes can substantially alleviate the membrane shrinkage during drying treatment. All of the prepared Pluronic F127/PES nanofiltration membranes can completely reject Alcian blue with a molecular weight of 1299. The water permeance of Pluronic F127/PES nanofiltration membrane at W(F127)/W(PES) of 80% is as high as 176.2 L/(m(2) h MPa). After long-term immersion into sodium hypochlorite solution, Pluronic F127/PES nanofiltration membranes still keep over 95.7% rejection of Alcian blue. |
英文摘要 | Pluronic F127/polyethersulfone (PES) blend nanofiltration membranes were fabricated by varying polymer weight ratios Of W-F127/W-PES in casting solutions from 0.0 to 100.0 wt %. The initial wet membranes prepared via the phase inversion method were post treated by drying at room temperature and then immersion into water for rewetting to obtain Pluronic F127/PES nanofiltration membranes. Membrane shrinkage and swelling, cross section and surface morphologies, water uptake, surface hydrophilicity, X-ray diffraction pattern, water flux, and rejection of dyes for Pluronic F127/PES nanofiltration membranes were investigated The introduction of pluronic F127 into PES membranes can substantially alleviate the membrane shrinkage during drying treatment. All of the prepared Pluronic F127/PES nanofiltration membranes can completely reject Alcian blue with a molecular weight of 1299. The water permeance of Pluronic F127/PES nanofiltration membrane at W-F127/W-PES of 80% is as high as 176.2 L/(m(2) h MPa). After long-term immersion into sodium hypochlorite solution, Pluronic F127/PES nanofiltration membranes still keep over 95.7% rejection of Alcian blue. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Engineering, Chemical |
研究领域[WOS] | Engineering |
关键词[WOS] | SOLVENT-RESISTANT NANOFILTRATION ; ULTRAFILTRATION MEMBRANES ; POLYETHERSULFONE MEMBRANES ; COMPOSITE MEMBRANES ; MOLECULAR-LEVEL ; HOLLOW FIBERS ; PERFORMANCE ; F127 ; SPECTROSCOPY |
收录类别 | SCI |
原文出处 | |
语种 | 英语 |
WOS记录号 | WOS:000289341200052 |
公开日期 | 2013-11-28 |
版本 | 出版稿 |
源URL | [http://ir.ipe.ac.cn/handle/122111/6347] ![]() |
专题 | 过程工程研究所_研究所(批量导入) |
作者单位 | 1.Tianjin Univ, Sch Chem Engn & Technol, Minist Educ, Key Lab Green Technol, Tianjin 300072, Peoples R China 2.Chinese Acad Sci, Inst Proc Engn, Natl Key Lab Biochem Engn, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Yan,Su, Yanlei,Chen, Wenjuan,et al. A Feasible Post-Treatment of Drying and Rewetting for Preparation of High-Flux Pluronic F127/Polyethersulfone Nanofiltration Membranes[J]. INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH,2011,50(8):4678-4685. |
APA | Zhang, Yan,Su, Yanlei,Chen, Wenjuan,Peng, Jinming,Dong, Yanan,&Jiang, Zhongyi.(2011).A Feasible Post-Treatment of Drying and Rewetting for Preparation of High-Flux Pluronic F127/Polyethersulfone Nanofiltration Membranes.INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH,50(8),4678-4685. |
MLA | Zhang, Yan,et al."A Feasible Post-Treatment of Drying and Rewetting for Preparation of High-Flux Pluronic F127/Polyethersulfone Nanofiltration Membranes".INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH 50.8(2011):4678-4685. |
入库方式: OAI收割
来源:过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。