In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium
文献类型：期刊论文
| 作者 | Sun CY(孙彩云) ; Xie JJ(谢季佳); Wu XL(武晓雷); Hong YS(洪友士); Liu G; Lu J; Lu K
|
| 刊名 | 材料热处理学报
 |
| 出版日期 | 2004 |
| 卷号 | 25期号:5II页码:1242-1246 |
| 关键词 | nanocrystalline intermetallic compound surface layer deformation diffusion |
| ISSN号 | 1009-6264 |
| 中文摘要 | The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC)layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 μm thick and consisted of the intermetallic compound FeCr with an average grain size of 25+10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa. |
| 收录类别 | EI ; CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:1847864 |
| 公开日期 | 2014-01-20 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/47743]  |
| 专题 | 力学研究所_力学所知识产出(1956-2008) |
| 推荐引用方式 GB/T 7714 | Sun CY,Xie JJ,Wu XL,et al. In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium[J]. 材料热处理学报,2004,25(5II):1242-1246. |
| APA | Sun CY.,Xie JJ.,Wu XL.,Hong YS.,Liu G.,...&Lu K.(2004).In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium.材料热处理学报,25(5II),1242-1246. |
| MLA | Sun CY,et al."In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium".材料热处理学报 25.5II(2004):1242-1246. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。