180 degrees domain structure and its evolution in Ca0.28Ba0.72Nb2O6 ferroelectric single crystals of tungsten bronzes structure
文献类型：期刊论文
| 作者 | Lu, CJ ; Nie, CJ ; Duan, XF ; Li, JQ ; Zhang, HJ ; Wang, JY |
| 刊名 | APPLIED PHYSICS LETTERS
 |
| 出版日期 | 2006 |
| 卷号 | 88期号:20 |
| 关键词 | CAXBA1-XNB2O6 X=0.28 BARIUM-TITANATE DIFFRACTION GROWTH CBN-28 |
| ISSN号 | 0003-6951 |
| 通讯作者 | Lu, CJ: Hubei Univ, Dept Mat Sci & Engn, Wuhan 430062, Peoples R China. |
| 中文摘要 | Ferroelectric domain structure and its evolution in uniaxial relaxor Ca0.28Ba0.72Nb2O6 single crystals were investigated using transmission electron microscopy. It was found that there exists a high density of 180 degrees domain walls in the crystals. The domains appear predominantly spike shaped along the polar axis and have a typical diameter of 50-500 nm. Domain wall motion was occasionally induced by electron beam irradiation. Macrodomains-to-microdomains switching has been observed corresponding to the normal-to-relaxor ferroelectrics transition during an in situ heating experiments. At temperature just below ferroelectric phase transition temperature T-C, zero-field-cooled needlelike nanodomains were also observed. (c) 2006 American Institute of Physics. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-17 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/32637]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Lu, CJ,Nie, CJ,Duan, XF,et al. 180 degrees domain structure and its evolution in Ca0.28Ba0.72Nb2O6 ferroelectric single crystals of tungsten bronzes structure[J]. APPLIED PHYSICS LETTERS,2006,88(20). |
| APA | Lu, CJ,Nie, CJ,Duan, XF,Li, JQ,Zhang, HJ,&Wang, JY.(2006).180 degrees domain structure and its evolution in Ca0.28Ba0.72Nb2O6 ferroelectric single crystals of tungsten bronzes structure.APPLIED PHYSICS LETTERS,88(20). |
| MLA | Lu, CJ,et al."180 degrees domain structure and its evolution in Ca0.28Ba0.72Nb2O6 ferroelectric single crystals of tungsten bronzes structure".APPLIED PHYSICS LETTERS 88.20(2006). |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。