A new method in preparation of colloidal semiconductor nanocrystals
文献类型：期刊论文
| 作者 | Wu, ZY ; Fu, LM ; Wang, YM ; Wang, YT ; Miao, YM ; Li, QS ; Zou, BS |
| 刊名 | PROGRESS IN CHEMISTRY
 |
| 出版日期 | 2004 |
| 卷号 | 16期号:1页码:1 |
| 关键词 | CDSE NANOCRYSTALS QUANTUM DOTS CORE/SHELL NANOCRYSTALS ALTERNATIVE ROUTES II-VI GROWTH MONODISPERSE EMISSION CLUSTERS POLYMER |
| ISSN号 | 1005-281X |
| 通讯作者 | Wu, ZY: Chinese Acad Sci, Inst Phys, POB 603, Beijing 100080, Peoples R China. |
| 中文摘要 | The electric resistance and capacitance of different sized free-standing ZnFe2O4 nanocrystals were measured under pressure up to 20 GPa in a diamond anvil cell at ambient temperature. The experimental results demonstrate that phase transition takes place at 5.5 GPa and 8.9 GPa for 5 nm and 70 nm nanocrystals, respectively, in contrast to the prediction of scaling theory on the phase transformation of semiconductor nanocrystals. When the pressure exceeds the phase transition pressure, the resistance and capacitance of ZnFe2O4 nanocrystals decrease exponentially with pressure following the relationships R similar to exp(-CRP) and C similar to exp(-CCP), where C-R = 0.4739 GPa(-1) and C-C = 0.5263 GPa(-1) for 5nm ZnFe2O4 crystals, CR = 0.1667 GPa(-1) and C-C = 0.2447 for the 70 nm one. It is interesting that the pressure-dependent resistance profile changed significantly when the samples were treated with minor water before pressing. The nanocrystals follow the rule that small particle grows and largo particle decreases under pressure. |
| 收录类别 | SCI |
| 语种 | 中文 |
| 公开日期 | 2013-09-17 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/33062]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wu, ZY,Fu, LM,Wang, YM,et al. A new method in preparation of colloidal semiconductor nanocrystals[J]. PROGRESS IN CHEMISTRY,2004,16(1):1. |
| APA | Wu, ZY.,Fu, LM.,Wang, YM.,Wang, YT.,Miao, YM.,...&Zou, BS.(2004).A new method in preparation of colloidal semiconductor nanocrystals.PROGRESS IN CHEMISTRY,16(1),1. |
| MLA | Wu, ZY,et al."A new method in preparation of colloidal semiconductor nanocrystals".PROGRESS IN CHEMISTRY 16.1(2004):1. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。