Co/Pt multilayers with large coercivity and small grains

文献类型:期刊论文

作者Shan, R ; Gao, TR ; Zhou, SM ; Wu, XS ; Fang, YK ; Han, BS
刊名JOURNAL OF APPLIED PHYSICS
出版日期2006
卷号99期号:6
关键词PERPENDICULAR MAGNETIC-ANISOTROPY LAYERED STRUCTURES FILMS MICROSTRUCTURE
ISSN号0021-8979
通讯作者Zhou, SM: Fudan Univ, Surface Phys Lab, Natl Key Lab, Shanghai 200433, Peoples R China.
中文摘要Multilayers of [Co/Pt](20), with t(Co)/t(Pt)center dot 7 and the period Lambda in the range of 0.27-0.69 nm, and [Co(0.46 nm)/Pt(0.07-0.14 nm)](20) have been prepared by sputtering at low deposition rates and a high Ar pressure of 7.8 Pa. Structure and magnetic properties were characterized by x-ray diffraction, transmission electron microscopy, magnetometry measurements, and magnetic force microscopy. Column structure, coherent stacking of Co and Pt layers, and small grains have been observed. The average atomic interplane distance d(111) changes with the constituent layer thickness. In the first series of Co/Pt multilayers, the out-of-plane coercivity gradually increases to reach a maximum, with the bilayer period increasing from 0 to 0.58 nm, and decreases with further increasing period. For the second series, the out-of-plane coercivity increases to reach a maximum of 6.5 kOe with t(Pt) increasing from 0.07 to 0.13 nm and decreases with further increasing t(Pt). In order to explain the strong magnetic perpendicular anisotropy, the magnetoelastic energy of CoPt alloy layers must be taken into account.
收录类别SCI
语种英语
公开日期2013-09-17
源URL[http://ir.iphy.ac.cn/handle/311004/34764]  
专题物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式
GB/T 7714
Shan, R,Gao, TR,Zhou, SM,et al. Co/Pt multilayers with large coercivity and small grains[J]. JOURNAL OF APPLIED PHYSICS,2006,99(6).
APA Shan, R,Gao, TR,Zhou, SM,Wu, XS,Fang, YK,&Han, BS.(2006).Co/Pt multilayers with large coercivity and small grains.JOURNAL OF APPLIED PHYSICS,99(6).
MLA Shan, R,et al."Co/Pt multilayers with large coercivity and small grains".JOURNAL OF APPLIED PHYSICS 99.6(2006).

入库方式: OAI收割

来源:物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。