Density effect on critical current density and flux pinning properties of polycrystalline SmFeAsO1-xFx superconductor

文献类型:期刊论文

作者Ding, Y ; Sun, Y ; Zhuang, JC ; Cui, LJ ; Shi, ZX ; Sumption, MD ; Majoros, M ; Susner, MA ; Kovacs, CJ ; Li, GZ ; Collings, EW ; Ren, ZA
刊名SUPERCONDUCTOR SCIENCE & TECHNOLOGY
出版日期2011
卷号24期号:12
关键词LAYERED QUATERNARY COMPOUND YBA2CU3O7-DELTA MAGNETIZATION TEMPERATURE CRYSTALS
ISSN号0953-2048
通讯作者Ding, Y: Southeast Univ, Dept Phys, Nanjing 211189, Peoples R China.
中文摘要A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The superconducting volume fraction, the critical current densities J(cm) and the flux pinning force densities F-p were estimated from the magnetization measurements. Experimental results show that: (1) the superconducting volume fraction increases with the increasing of sample density; (2) the J(cm) values have a similar trend except for the sample with very high density due to different connectivity and pinning mechanisms, moreover, the J(cm)(B) curve develops a peak effect at approximately the same field at which the high density sample shows a kink; (3) the F-p(B) curve of the high density sample shows a low-field peak and a high-field peak at several temperatures, which can be explained by improved intergranular current, while only one peak can be observed in F-p(B) of the low density samples. Based on the scaling behaviour of flux pinning force densities, the main intragranular pinning is normal point pinning.
收录类别SCI
资助信息Natural Science Foundation of China; Ministry of Science and Technology of China [2011CBA00105]; Important Project [2011seuzd09]; US Department of Energy, Division of High Energy Physics [DE-FG02-95ER40900]; Scientific Research Foundation of the Graduate School of Southeast University [YBJJ0933]
语种英语
公开日期2013-09-17
源URL[http://ir.iphy.ac.cn/handle/311004/35714]  
专题物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式
GB/T 7714
Ding, Y,Sun, Y,Zhuang, JC,et al. Density effect on critical current density and flux pinning properties of polycrystalline SmFeAsO1-xFx superconductor[J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY,2011,24(12).
APA Ding, Y.,Sun, Y.,Zhuang, JC.,Cui, LJ.,Shi, ZX.,...&Ren, ZA.(2011).Density effect on critical current density and flux pinning properties of polycrystalline SmFeAsO1-xFx superconductor.SUPERCONDUCTOR SCIENCE & TECHNOLOGY,24(12).
MLA Ding, Y,et al."Density effect on critical current density and flux pinning properties of polycrystalline SmFeAsO1-xFx superconductor".SUPERCONDUCTOR SCIENCE & TECHNOLOGY 24.12(2011).

入库方式: OAI收割

来源:物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。