Effect of Cu substitution on structure and magnetic properties of anisotropic SmCo ribbons
文献类型：期刊论文
| 作者 | Zhang, WY ; Zhang, XD ; Yang, YC ; Shen, BG |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2003 |
| 卷号 | 353期号:1-2页码:274 |
| 关键词 | ABNORMAL TEMPERATURE-DEPENDENCE INTRINSIC-COERCIVITY FE MICROSTRUCTURE ALLOYS TEXTURE SM(CO ZR GD |
| ISSN号 | 0925-8388 |
| 通讯作者 | Zhang, WY: Peking Univ, Sch Phys, Beijing 100871, Peoples R China. |
| 中文摘要 | Anisotropic SmCo7-xCux (x = 0-4.5) ribbons have been prepared by melt spinning at a low wheel speed of 5 m/s. Scanning electron microscopy results show that Cu-free and Cu-containing ribbons consist of equiaxed and columnar dendrite grains, respectively. The arrangement of columnar dendrite grains of the ribbons was found to be more ordered with increasing Cu content x. Together with the results of magnetic measurement, it is derived that Cu substitution is helpful to enhance the degree of preferred orientation of the c-axis of the columnar dendrite grains parallel to the longitudinal direction of the ribbons. In this way the rectangularity of demagnetization curves and the remanence ratio (defined as the ratio of remanent magnetization to saturation magnetization) of the samples are significantly improved. A remanence ratio of 0.90, which is close to that of sintered SmCo magnets, has been achieved in the ribbons with x = 2.5. Because the domain-wall-energy gradient between the 1:5 and 2:17 phases, which determines the value of the coercive force arising from the domain wall pinning. may increase with x, the coercivity of the samples with xless than or equal to3.5 increases strongly with x. Without heat treatment, a coercive force (H-i(c)) of up to 9.2 kOe is obtained in the ribbons with x = 3.5. (C) 2002 Elsevier Science B.V. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-17 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/36395]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhang, WY,Zhang, XD,Yang, YC,et al. Effect of Cu substitution on structure and magnetic properties of anisotropic SmCo ribbons[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2003,353(1-2):274. |
| APA | Zhang, WY,Zhang, XD,Yang, YC,&Shen, BG.(2003).Effect of Cu substitution on structure and magnetic properties of anisotropic SmCo ribbons.JOURNAL OF ALLOYS AND COMPOUNDS,353(1-2),274. |
| MLA | Zhang, WY,et al."Effect of Cu substitution on structure and magnetic properties of anisotropic SmCo ribbons".JOURNAL OF ALLOYS AND COMPOUNDS 353.1-2(2003):274. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。