Effects of oxygen pressure on lattice parameter, orientation, surface morphology and deposition rate of (Ba0.02Sr0.98)TiO3 thin films grown on MgO substrate by pulsed laser deposition
文献类型：期刊论文
| 作者 | Wang, C ; Cheng, BL ; Wang, SY ; Lu, HB ; Zhou, YL ; Chen, ZH ; Yang, GZ |
| 刊名 | THIN SOLID FILMS
 |
| 出版日期 | 2005 |
| 卷号 | 485期号:1-2页码:82 |
| 关键词 | PHASE SHIFTERS SRTIO3 THICKNESS TITANATE ABLATION QUALITY OXIDES FLUX |
| ISSN号 | 0040-6090 |
| 通讯作者 | Cheng, BL: Chinese Acad Sci, Inst Phys, Beijing 100080, Peoples R China. |
| 中文摘要 | (Ba0.02Sr0.98)TiO3 thin films were grown on MgO substrate by pulsed laser deposition (PLD) techniques at various oxygen pressures from 40 to 10(-3) Pa. Effects of oxygen pressure on lattice parameter, orientation, surface morphology and deposition rate of the thin films were investigated. X-ray diffraction patterns indicate that, with decreasing oxygen pressure, crystal orientation of the thin films develops from (110) preferred orientation to random orientation, and finally to perfectly (001) texture. Meantime, lattice parameter of the thin films increases with decreasing oxygen pressure. Especially, perfectly (001)-oriented (Ba0.02Sr0.98)TiO3 thin film was obtained under oxygen pressure of 10-3 Pa at substrate temperature of 850 degrees C, in spite of the large lattice mismatch of about 8% between (Ba0.02Sr0.98)TiO3 and MgO. Atomic force microscopy images show that all the thin films have granular structure and the thin film grown at 10(-3) Pa has much more homogeneous grain size distribution compared to all the other thin films. Moreover, the films grown at oxygen pressures of 1 and 10(-1) Pa have more smooth surfaces, and the deposition rate of thin film increases with decreasing oxygen pressure. (c) 2005 Published by Elsevier B.V. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-17 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/36780]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang, C,Cheng, BL,Wang, SY,et al. Effects of oxygen pressure on lattice parameter, orientation, surface morphology and deposition rate of (Ba0.02Sr0.98)TiO3 thin films grown on MgO substrate by pulsed laser deposition[J]. THIN SOLID FILMS,2005,485(1-2):82. |
| APA | Wang, C.,Cheng, BL.,Wang, SY.,Lu, HB.,Zhou, YL.,...&Yang, GZ.(2005).Effects of oxygen pressure on lattice parameter, orientation, surface morphology and deposition rate of (Ba0.02Sr0.98)TiO3 thin films grown on MgO substrate by pulsed laser deposition.THIN SOLID FILMS,485(1-2),82. |
| MLA | Wang, C,et al."Effects of oxygen pressure on lattice parameter, orientation, surface morphology and deposition rate of (Ba0.02Sr0.98)TiO3 thin films grown on MgO substrate by pulsed laser deposition".THIN SOLID FILMS 485.1-2(2005):82. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。