Ferromagnetism of Mn-doped GaN polycrystalline powders
文献类型：期刊论文
| 作者 | Li, H ; Song, B ; Bao, HQ ; Wang, G ; Wang, WJ ; Chen, XL |
| 刊名 | JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
 |
| 出版日期 | 2009 |
| 卷号 | 321期号:3页码:222 |
| 关键词 | GAMNN MAGNETIC SEMICONDUCTOR MOLECULAR-BEAM-EPITAXY TEMPERATURE FERROMAGNETISM THIN-FILMS LAYERS GA1-XMNXN ZNO |
| ISSN号 | 0304-8853 |
| 通讯作者 | Chen, XL: Chinese Acad Sci, Inst Phys, Beijing Natl Lab Condensed Matter Phys, POB 603, Beijing 100190, Peoples R China. |
| 中文摘要 | Ferroelectric copolymer thin film PVDF-TrFE was deposited by spin coating method, and then annealed for the improved crystallization. The XRD and AFM measurements showed that as-formed PVDF-TrFE thin film was composed of the nanocrystallines with 50-80 nm in size and some amorphous phases. Meanwhile, as-formed PVDF-TrFE thin films also show a good polarization inversion property with a switch current of similar to 2.0 mu A at a coercive field 40 MV/m. Electron emission testing results showed that under a continuous excitation of applied voltage pulses, PVDF-TrFE thin films exhibited an expected electron emission ability with emission current range of 0.08-0.52 AA, and the related electron emission mechanism was discussed. |
| 收录类别 | SCI |
| 资助信息 | National Natural Science Foundation [50372081, 50502039]; Hundred Talents Project of the Chinese Academy of Sciences |
| 语种 | 英语 |
| 公开日期 | 2013-09-17 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/38113]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Li, H,Song, B,Bao, HQ,et al. Ferromagnetism of Mn-doped GaN polycrystalline powders[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS,2009,321(3):222. |
| APA | Li, H,Song, B,Bao, HQ,Wang, G,Wang, WJ,&Chen, XL.(2009).Ferromagnetism of Mn-doped GaN polycrystalline powders.JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS,321(3),222. |
| MLA | Li, H,et al."Ferromagnetism of Mn-doped GaN polycrystalline powders".JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS 321.3(2009):222. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。