GROWTH OF LARGE-DOMAIN YBA2CU3OX WITH NEW SEEDING CRYSTALS OF CANDALO4 AND SRLAGAO4
文献类型:期刊论文
作者 | SHI, DL ; LAHIRI, K ; HULL, JR ; LEBLANC, D ; LEBLANC, MAR ; DABKOWSKI, A ; CHANG, Y ; JIANG, Y ; ZHANG, Z ; FAN, H |
刊名 | PHYSICA C
![]() |
出版日期 | 1995 |
卷号 | 246期号:3-4页码:253 |
关键词 | MELT-PROCESSED YBA2CU3OX SUPERCONDUCTORS MICROSTRUCTURE |
ISSN号 | 0921-4534 |
通讯作者 | SHI, DL: UNIV CINCINNATI,DEPT MAT SCI & ENGN,CINCINNATI,OH 45211, USA. |
中文摘要 | Single crystals of CaNdAlO4 and SrLaGaO4 were used as seeds to grow large domains of YBa2Cu3Ox for levitation applications. These crystals have high melting temperatures (> 1500 degrees C) and similar lattice structures to that of YBa2Cu3Ox. In a seeded melt-texturing method developed previously, the single crystals of CaNdAlO4, SrLaGaO4, and NdBa2Cu3Ox were used as seeds for comparison. After melt processing, scanning electron microscopy analysis did not reveal any major differences in all these seeded melt-textured samples. However, the levitation forces in the samples seeded with single crystals of CaNdAlO4 and SrLaGaO4 increased considerably compared to that of the sample seeded with NdBa2Cu3Ox. A model is proposed to describe the domain growth mechanism during seeded melt processing. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
源URL | [http://ir.iphy.ac.cn/handle/311004/38968] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | SHI, DL,LAHIRI, K,HULL, JR,et al. GROWTH OF LARGE-DOMAIN YBA2CU3OX WITH NEW SEEDING CRYSTALS OF CANDALO4 AND SRLAGAO4[J]. PHYSICA C,1995,246(3-4):253. |
APA | SHI, DL.,LAHIRI, K.,HULL, JR.,LEBLANC, D.,LEBLANC, MAR.,...&FAN, H.(1995).GROWTH OF LARGE-DOMAIN YBA2CU3OX WITH NEW SEEDING CRYSTALS OF CANDALO4 AND SRLAGAO4.PHYSICA C,246(3-4),253. |
MLA | SHI, DL,et al."GROWTH OF LARGE-DOMAIN YBA2CU3OX WITH NEW SEEDING CRYSTALS OF CANDALO4 AND SRLAGAO4".PHYSICA C 246.3-4(1995):253. |
入库方式: OAI收割
来源:物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。