HIGH PRESSURE SYNTHESIS OF HIGH Tc A15 Nb3Si
文献类型:期刊论文
作者 | WANG Yaoji ; WANG Wenkui ; HE Shouan ; H. Iwasaki |
刊名 | Chin. Phys. Lett.
![]() |
出版日期 | 1987 |
卷号 | 4期号:1页码:44 |
中文摘要 | The A15 Nb3Si with a smaller lattice parameter (a=0.5093nm) has been synthesized from the amorphous Nb77Si23 alloy under high pressure by using Bridgman anvils apparatus. Superconductivity measurements shoued that the A15 phase produced from Nb77Si23 has the highest Tc(19.1K) among all that can be obtained from Nb-Si alloys. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
源URL | [http://ir.iphy.ac.cn/handle/311004/39230] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | WANG Yaoji,WANG Wenkui,HE Shouan,et al. HIGH PRESSURE SYNTHESIS OF HIGH Tc A15 Nb3Si[J]. Chin. Phys. Lett.,1987,4(1):44. |
APA | WANG Yaoji,WANG Wenkui,HE Shouan,&H. Iwasaki.(1987).HIGH PRESSURE SYNTHESIS OF HIGH Tc A15 Nb3Si.Chin. Phys. Lett.,4(1),44. |
MLA | WANG Yaoji,et al."HIGH PRESSURE SYNTHESIS OF HIGH Tc A15 Nb3Si".Chin. Phys. Lett. 4.1(1987):44. |
入库方式: OAI收割
来源:物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。