Layered monodiphosphate Li9V3(P2O7)(3)(PO4)(2): A novel cathode material for lithium-ion batteries
文献类型：期刊论文
| 作者 | Kuang, Q ; Xu, JT ; Zhao, YM ; Chen, XL ; Chen, LQ |
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2011 |
| 卷号 | 56期号:5页码:2201 |
| 关键词 | ELECTROCHEMICAL PROPERTIES PHOSPHATES IRON |
| ISSN号 | 0013-4686 |
| 通讯作者 | Zhao, YM: S China Univ Technol, Sch Phys, Guangzhou 510640, Peoples R China. |
| 中文摘要 | Single phase Li9V3(P2O7)(3)(PO4)(2) is synthesized at 750 degrees C via solid-state reaction method for the first time. The Rietveld refinement results show that the trigonal system (space group: P $(3) over bar $ c1) with the lattice parameters a = 0.9724 nm, c = 1.3596 nm are obtained. Its intrinsic electrical conductivity of 1.43 x 10(-8) S cm(-1) is higher than that of LiFePO4 and as the same order of Li3V2(PO3)(4.) The electrochemical measurement results show that there are two plateaus (3.77V and 4.51 V) and three plateaus (3.77 V. 4.51 V and 4.75V) in the potential ranges of 2.0-4.6 V and 2.0-4.8V, respectively. In the range of 2.0-4.6 V. two discharge plateaus (4.46V and 3.74V) can be observed and 110 mAh g(-1) of discharge capacity is achieved. The Rietveld refinement result of the X-ray diffraction (XRD) data at the end of discharge after the first cycle suggests that the structural reversibility can be retained during electrochemical reactions in Li9V3(P2O7)(3)(PO4)(2). In the range of 2.0-4.8 V. almost six lithium ions are extracted and the trigonal structure is still recovered after 30 cycles. Therefore, this novel layered vanadium monodiphosphate offers a promising candidate as cathode material for lithium-ion batteries. (C) 2010 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 资助信息 | NSFC [50772039]; NSFC Committee of China and the Foundation [07118058]; Science and Technology Bureau of Guangdong Government |
| 语种 | 英语 |
| 公开日期 | 2013-09-18 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/40746]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Kuang, Q,Xu, JT,Zhao, YM,et al. Layered monodiphosphate Li9V3(P2O7)(3)(PO4)(2): A novel cathode material for lithium-ion batteries[J]. ELECTROCHIMICA ACTA,2011,56(5):2201. |
| APA | Kuang, Q,Xu, JT,Zhao, YM,Chen, XL,&Chen, LQ.(2011).Layered monodiphosphate Li9V3(P2O7)(3)(PO4)(2): A novel cathode material for lithium-ion batteries.ELECTROCHIMICA ACTA,56(5),2201. |
| MLA | Kuang, Q,et al."Layered monodiphosphate Li9V3(P2O7)(3)(PO4)(2): A novel cathode material for lithium-ion batteries".ELECTROCHIMICA ACTA 56.5(2011):2201. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。