Magnetic microstructures of 2 : 17 type Sm (Co, Fe, Cu, Zr)(z) magnets detected by magnetic force microscopy
文献类型:期刊论文
作者 | Xia, AL ; Guo, ZH ; Wei, L ; Han, BS |
刊名 | JOURNAL OF RARE EARTHS
![]() |
出版日期 | 2006 |
卷号 | 24期号:2页码:214 |
关键词 | DOMAIN-STRUCTURE STRIPS RANGE NDFEB TIPS MFM |
ISSN号 | 1002-0721 |
通讯作者 | Han, BS: Chinese Acad Sci, Inst Phys, State Key Lab Magnstism, Beijing Natl Lab Condensed Phys, POB 603, Beijing 100080, Peoples R China. |
中文摘要 | The magnetic microstructures of 2: 17 type Sm (Co, Fe, Cu, Zr). magnets were detected by magnetic force microscopy. Comparing the microstructures of the specimens coated with and without Ta thin film before and after heat-treatment, it is found that: (a) as a protection layer, Ta coating layer about 20 nm thick can effectively restrain Sm volatilization under high temperature; (b) the stress built in the 2: 17 type Sm-Co, magnets during specimen preparation only affects some local parts of the domain structures; (c) the magnetic microstructures vary largely for specimens heat-treated at high temperature without Ta film coating due to Sm volatilization. In addition, by comparing with high coercivity Fe-Pt point tips, It is found that the Co-Cr thin-film tips are not suitable for detecting the magnetic microstructures of strong permanent magnets. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-18 |
源URL | [http://ir.iphy.ac.cn/handle/311004/41253] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Xia, AL,Guo, ZH,Wei, L,et al. Magnetic microstructures of 2 : 17 type Sm (Co, Fe, Cu, Zr)(z) magnets detected by magnetic force microscopy[J]. JOURNAL OF RARE EARTHS,2006,24(2):214. |
APA | Xia, AL,Guo, ZH,Wei, L,&Han, BS.(2006).Magnetic microstructures of 2 : 17 type Sm (Co, Fe, Cu, Zr)(z) magnets detected by magnetic force microscopy.JOURNAL OF RARE EARTHS,24(2),214. |
MLA | Xia, AL,et al."Magnetic microstructures of 2 : 17 type Sm (Co, Fe, Cu, Zr)(z) magnets detected by magnetic force microscopy".JOURNAL OF RARE EARTHS 24.2(2006):214. |
入库方式: OAI收割
来源:物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。