MAGNETIC-PROPERTIES OF Y-3(FE,TI)(29)

文献类型:期刊论文

作者Li, HS ; COURTOIS, D ; CADOGAN, JM ; HU, BP ; ZHAN, WS
刊名IEEE TRANSACTIONS ON MAGNETICS
出版日期1995
卷号31期号:6页码:3680
关键词IRON
ISSN号0018-9464
通讯作者LI, HS: UNIV NEW S WALES,SCH PHYS,SYDNEY,NSW 2052,AUSTRALIA.
中文摘要Magnetization curves have been measured on both epoxy resin-fixed random and magnetically aligned powder samples of Y-3(Fe27.4Ti1.6) at temperatures of 1.5, 100, 200 and 293 K with an applied magnetic field up to 7 T. The X-ray diffraction pattern of the magnetically aligned Y-3(Fe27.4Ti1.6) sample suggests a planar easy magnetization direction (referred to the underlying hexagonal CaCu5 structure). The room temperature anisotropy field deduced from these magnetization data is 3.0(5) T and reaches 7.3(5) T at 1.5 K, The average Fe magnetic moment at 7.0 T is 1.44(1) mu(B) at 293K and 1.86(1) mu(B) at 1.5 K, respectively.
收录类别SCI
语种英语
公开日期2013-09-18
源URL[http://ir.iphy.ac.cn/handle/311004/41540]  
专题物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式
GB/T 7714
Li, HS,COURTOIS, D,CADOGAN, JM,et al. MAGNETIC-PROPERTIES OF Y-3(FE,TI)(29)[J]. IEEE TRANSACTIONS ON MAGNETICS,1995,31(6):3680.
APA Li, HS,COURTOIS, D,CADOGAN, JM,HU, BP,&ZHAN, WS.(1995).MAGNETIC-PROPERTIES OF Y-3(FE,TI)(29).IEEE TRANSACTIONS ON MAGNETICS,31(6),3680.
MLA Li, HS,et al."MAGNETIC-PROPERTIES OF Y-3(FE,TI)(29)".IEEE TRANSACTIONS ON MAGNETICS 31.6(1995):3680.

入库方式: OAI收割

来源:物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。