Modification of the external surface of ZSM-5 by a metal surfactant
文献类型：期刊论文
| 作者 | Hu, ZS ; Wei, LH ; Dong, JX ; Wang, JR ; Chen, SY ; Peng, SY |
| 刊名 | MICROPOROUS AND MESOPOROUS MATERIALS
 |
| 出版日期 | 1999 |
| 卷号 | 28期号:1页码:49 |
| 关键词 | METHANOL AMINATION ZEOLITE SPECTROSCOPY CATALYSTS ACIDITY |
| ISSN号 | 1387-1811 |
| 通讯作者 | Hu, ZS: Logist Engn Coll, Dept Petrochem, Chongqing 400042, Peoples R China. |
| 中文摘要 | A nanocrystalline (NC) sample was prepared by quenching a Hf11Ni89 alloy with the melt-pinning technique A randomly oriented HfNi5, nanophase with an average grain size of about 10 nm was formed by this process A an extension of our previous work on the as-quenched state of this NC Hf-Ni alloy, here we use DSC and XRD to report on a thermal stability study of samples pre-annealed at 340 degrees C for different periods of time t(a) up to 510 min. Thc pre-annealing was performed under conditions: that did not result in a change of the grain size. Similarly to the as-quenched state of the NC HfNi5 alloy, two exothermal peaks appear in the DSC curve for the pre-annealed NC samples on heating at a constant heating rate. The two peaks may also be attributed to a grain-growth process of the HfNi5 nanophase prior to a precipitation process of a Ni solid solution phase. Activation energies for the two processes were calculated by using the Kissinger equation, It was obtained that a pre-annealing treatment decreases the thermal stability of the NC sample, which was characterized by a reduction of the temperatures and the activation energies for thr grain-growth and the Ni precipitation processes. The DSC analysis revealed that the total excess energy of this highly non-equilibrium alloy and, specifically, the grain-boundary energy, decrease with increasing pre-annealing time. These changes in the parameters characterizing the thermal stability of the NC HfNi5 alloy are discussed on the basis of observed modifications of the microstructure with the help of atomic diffusion processes and, also, of magnetic measurements on pre-annealed samples described elsewhere. (C) 1999 Acta Metallurgica Inc. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-18 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/42219]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Hu, ZS,Wei, LH,Dong, JX,et al. Modification of the external surface of ZSM-5 by a metal surfactant[J]. MICROPOROUS AND MESOPOROUS MATERIALS,1999,28(1):49. |
| APA | Hu, ZS,Wei, LH,Dong, JX,Wang, JR,Chen, SY,&Peng, SY.(1999).Modification of the external surface of ZSM-5 by a metal surfactant.MICROPOROUS AND MESOPOROUS MATERIALS,28(1),49. |
| MLA | Hu, ZS,et al."Modification of the external surface of ZSM-5 by a metal surfactant".MICROPOROUS AND MESOPOROUS MATERIALS 28.1(1999):49. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。