Multilayered Si/Ni nanosprings and their magnetic properties
文献类型：期刊论文
| 作者 | He, YP ; Fu, JX ; Zhang, Y ; Zhao, YP ; Zhang, LJ ; Xia, AL ; Cai, JW |
| 刊名 | SMALL
 |
| 出版日期 | 2007 |
| 卷号 | 3期号:1页码:153 |
| 关键词 | GLANCING ANGLE DEPOSITION THIN-FILMS NANOWIRE HETEROSTRUCTURES NANOPILLAR ARRAYS CARBON NANOTUBES BUILDING-BLOCKS GROWTH DEVICES HETEROJUNCTIONS MICROSTRUCTURE |
| ISSN号 | 1613-6810 |
| 通讯作者 | Zhao, YP: Univ Georgia, Dept Phys & Astron, Athens, GA 30602 USA. |
| 中文摘要 | A two-turn, eight-armed, rectangular Si/Ni heterogeneous nanospring structure on Si(100) has been fabricated using a multilayer glancing-angle deposition technique. The multilayered nanosprings with a height of approximate to 1.98 mu m were composed of alternating layers of amorphous Si nanorods approximate to 580 nm in length and face-centered cubic Ni nanorods approximate to 420 nm in length, both with a diameter of approximate to 35 nm. The magnetic anisotropy of the nanosprings showed that the in-plane easy and hard axes were parallel and perpendicular to the Ni nanorod plane, respectively. The out-of-plane magnetic hysteresis loop was very sensitive to the applied magnetic field direction when rotating the nanosprings about their in-plane hard axis, and the magnetization measurement revealed that the nanosprings tilted at approximate to 7.5 degrees toward the plane of the Si nanorods. The magnetic anisotropy of the nanosprings is determined by their structure, and the experimental results can be interpreted by the shape anisotropy energy. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-18 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/42386]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | He, YP,Fu, JX,Zhang, Y,et al. Multilayered Si/Ni nanosprings and their magnetic properties[J]. SMALL,2007,3(1):153. |
| APA | He, YP.,Fu, JX.,Zhang, Y.,Zhao, YP.,Zhang, LJ.,...&Cai, JW.(2007).Multilayered Si/Ni nanosprings and their magnetic properties.SMALL,3(1),153. |
| MLA | He, YP,et al."Multilayered Si/Ni nanosprings and their magnetic properties".SMALL 3.1(2007):153. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。