The development of the phase composition in melt-spun Gd4Fe77.5B18.5 alloys with thermal treatment: a combined NMR and Mossbauer study

文献类型:期刊论文

作者Cheng, ZH ; Shen, BG ; Mao, MX ; Sun, JJ ; Wang, FW ; Li, FS ; Zhang, YD
刊名JOURNAL OF PHYSICS D-APPLIED PHYSICS
出版日期1997
卷号30期号:20页码:2812
关键词SHORT-RANGE ORDER MAGNETIC-PROPERTIES AMORPHOUS-ALLOYS HEAT-TREATMENT CRYSTALLINE GLASSES
ISSN号0022-3727
中文摘要The types of atomic short-range orders (SROs) in the amorphous alloy Gd4Fe77.5B18.5 and its crystallization products under different thermal-treatment conditions were investigated by means of spin-echo nuclear magnetic resonance (NMR) and Mossbauer spectroscopy. it was found that there exist two kinds of SROs in the amorphous alloy: body-centred tetragonal (BCT) Fe3B- and orthorhombic (o) Fe3B-like SROs. The crystallization products differ at various annealing temperatures: the sample annealed at 670 degrees C for 10 min consists of BCT Fe3B containing Gd and alpha-Fe, without the Gd2Fe14B phase; the sample annealed at 860 degrees C for 60 min contains BCT Fe3B, Gd1.1Fe4B4 and alpha-Fe; and the sample crystallized at 1010 degrees C for 10 min consists of Fe2B, alpha-Fe, Gd2Fe14B and Gd1.1Fe4B4. The experimental results indicate that the B-11 NMR peak shifts from 34.7 MHz for pure BCT Fe3B in the sample annealed at 860 degrees C for 60 min to 36.0 MHz for the sample annealed at 670 degrees C for 10 min and the relative intensity of the third Mossbauer sub-spectrum, corresponding to the Fe-III(8g) site of BCT Fe3B, is about 6% less than those of the other two. These facts can be explained in terms of the entering of Gd atoms into the BCT Fe3B phase.
收录类别SCI
语种英语
公开日期2013-09-23
源URL[http://ir.iphy.ac.cn/handle/311004/44992]  
专题物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式
GB/T 7714
Cheng, ZH,Shen, BG,Mao, MX,et al. The development of the phase composition in melt-spun Gd4Fe77.5B18.5 alloys with thermal treatment: a combined NMR and Mossbauer study[J]. JOURNAL OF PHYSICS D-APPLIED PHYSICS,1997,30(20):2812.
APA Cheng, ZH.,Shen, BG.,Mao, MX.,Sun, JJ.,Wang, FW.,...&Zhang, YD.(1997).The development of the phase composition in melt-spun Gd4Fe77.5B18.5 alloys with thermal treatment: a combined NMR and Mossbauer study.JOURNAL OF PHYSICS D-APPLIED PHYSICS,30(20),2812.
MLA Cheng, ZH,et al."The development of the phase composition in melt-spun Gd4Fe77.5B18.5 alloys with thermal treatment: a combined NMR and Mossbauer study".JOURNAL OF PHYSICS D-APPLIED PHYSICS 30.20(1997):2812.

入库方式: OAI收割

来源:物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。