Wear-resistant metal-carbon composite coating

文献类型:期刊论文

作者Uglov, VV ; Kuleshov, AK ; Rusalsky, DP ; Onate, JI ; Yang, SZ
刊名SURFACE & COATINGS TECHNOLOGY
出版日期2000
卷号128页码:150
关键词AMORPHOUS-CARBON ION-IMPLANTATION FILMS DEPOSITION LAYERS
ISSN号0257-8972
通讯作者Uglov, VV (reprint author), Belarussian State Univ, Pr F Scariny 4, Minsk 220080, Byelarus.
中文摘要Carbon coatings containing a metallic component (zirconium, tantalum) were deposited with ion assistance on AISI M2 steel samples using a SVETLYACHOK source. The coatings were studied by Auger electron spectroscopy (AES), transmission electron microscopy (TEM), Raman spectroscopy (RS) and pin-on-disc tribological tests. The results have shown that the carbon coatings contain up to 20 at.% of the metallic component. These coatings have an amorphous structure with sp(3)-type bonds. The presence of the coating on the surface of AISI M2 steel reduces the friction coefficient by a factor of five under the tribological conditions investigated. It is found that the tribological properties of the coatings deposited with the assistance of metal ions are significantly better than those coatings deposited with assistance of carbon ions. The latter coatings had carbon atoms with mixed sp(3)-sp(2) bonds. The deposited composite carbon coatings are stable at a temperature of 100 degrees C and allow a twofold improvement in the lifetime of fuel pump rods. (C) 2000 Elsevier Science S.A. All rights reserved.
收录类别SCI
语种英语
公开日期2013-09-23
源URL[http://ir.iphy.ac.cn/handle/311004/46633]  
专题物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式
GB/T 7714
Uglov, VV,Kuleshov, AK,Rusalsky, DP,et al. Wear-resistant metal-carbon composite coating[J]. SURFACE & COATINGS TECHNOLOGY,2000,128:150.
APA Uglov, VV,Kuleshov, AK,Rusalsky, DP,Onate, JI,&Yang, SZ.(2000).Wear-resistant metal-carbon composite coating.SURFACE & COATINGS TECHNOLOGY,128,150.
MLA Uglov, VV,et al."Wear-resistant metal-carbon composite coating".SURFACE & COATINGS TECHNOLOGY 128(2000):150.

入库方式: OAI收割

来源:物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。