Study on the structure and composition of anodic oxide films of aluminum
文献类型：期刊论文
| 作者 | Xu, T ; Zhao, JZ ; Cheng, JM ; Dang, HX |
| 刊名 | JOURNAL OF TRACE AND MICROPROBE TECHNIQUES
 |
| 出版日期 | 1997 |
| 卷号 | 15期号:4页码:521 |
| ISSN号 | 0733-4680 |
| 通讯作者 | Xu, T (reprint author), Chinese Acad Sci, Lanzhou Inst Chem Phys, Lab Solid Lubricat, Lanzhou 730000, Peoples R China. |
| 中文摘要 | The structure and composition of the porous anodic oxide films of aluminum (abbreviated AOFAl) formed in oxalic acid (I) and sulfuric acid (II) solutions, respectively, have been investigated by TEM, IR and TGA. The results show that the porous anodic oxide films consist of a large number of hexagonal cells with an irregularly round pore in the center of each cell wich penetrates vertically from surface to botton, while a barrier layer under the film directly contacts with an aluminum substrate in a scallop shape. The content of Al-2(C2O4)(3) and Al-2(SO4)(3) in AOFAl (I) and (II) are similar to 4.9 wt % and similar to 14.2 wt %, respectively; similar to 3.5 wt % water of crystallization of Al-2(SO4)(3),xH(2)O which can be evolved at rather low temperature (similar to 85 degrees C) enriches between the cells and under the barrier layer of AOFAl (II); after irradiation by the electron beam of TEM the water of crystallization is removed and voids are formed. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-09-24 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/53873]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Xu, T,Zhao, JZ,Cheng, JM,et al. Study on the structure and composition of anodic oxide films of aluminum[J]. JOURNAL OF TRACE AND MICROPROBE TECHNIQUES,1997,15(4):521. |
| APA | Xu, T,Zhao, JZ,Cheng, JM,&Dang, HX.(1997).Study on the structure and composition of anodic oxide films of aluminum.JOURNAL OF TRACE AND MICROPROBE TECHNIQUES,15(4),521. |
| MLA | Xu, T,et al."Study on the structure and composition of anodic oxide films of aluminum".JOURNAL OF TRACE AND MICROPROBE TECHNIQUES 15.4(1997):521. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。