Amorphous silicon-carbon nanospheres synthesized by chemical vapor deposition using cheap methyltrichlorosilane as improved anode materials for Li-ion batteries
文献类型：期刊论文
| 作者 | Zhang, ZL ; Zhang, MJ ; Wang, YH ; Tan, QQ ; Lv, X ; Zhong, ZY ; Li, H ; Su, FB |
| 刊名 | NANOSCALE
 |
| 出版日期 | 2013 |
| 卷号 | 5期号:12页码:5384 |
| ISSN号 | 2040-3364 |
| 通讯作者 | Wang, YH (reprint author), Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Beijing 100190, Peoples R China. |
| 中文摘要 | We report the preparation and characterization of amorphous silicon-carbon (Si-C) nanospheres as anode materials in Li-ion batteries. These nanospheres were synthesized by a chemical vapor deposition at 900 degrees C using methyltrichlorosilane (CH3SiCl3) as both the Si and C precursor, which is a cheap byproduct in the organosilane industry. The samples were characterized by X-ray diffraction, transmission electron microscopy, scanning electron microscopy, nitrogen adsorption, thermal gravimetric analysis, Raman spectroscopy, and X-ray photoelectron spectroscopy. It was found that the synthesized Si-C nanospheres composed of amorphous C (about 60 wt%) and Si (about 40 wt%) had a diameter of 400-600 nm and a surface area of 43.8 m(2) g(-1). Their charge capacities were 483.6, 331.7, 298.6, 180.6, and 344.2 mA h g(-1) at 50, 200, 500, 1000, and 50 mA g(-1) after 50 cycles, higher than that of the commercial graphite anode. The Si-C amorphous structure could absorb a large volume change of Si during Li insertion and extraction reactions and hinder the cracking or crumbling of the electrode, thus resulting in the improved reversible capacity and cycling stability. The work opens a new way to fabricate low cost Si-C anode materials for Li-ion batteries. |
| 资助信息 | National Natural Science Foundation of China [51272252]; State Key Laboratory of Multiphase Complex Systems of China [MPCS-2012-A-09]; Hundred Talents Program of the Chinese Academy of Sciences |
| 语种 | 英语 |
| 公开日期 | 2014-01-16 |
| 源URL | [http://ir.iphy.ac.cn/handle/311004/56767]  |
| 专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhang, ZL,Zhang, MJ,Wang, YH,et al. Amorphous silicon-carbon nanospheres synthesized by chemical vapor deposition using cheap methyltrichlorosilane as improved anode materials for Li-ion batteries[J]. NANOSCALE,2013,5(12):5384. |
| APA | Zhang, ZL.,Zhang, MJ.,Wang, YH.,Tan, QQ.,Lv, X.,...&Su, FB.(2013).Amorphous silicon-carbon nanospheres synthesized by chemical vapor deposition using cheap methyltrichlorosilane as improved anode materials for Li-ion batteries.NANOSCALE,5(12),5384. |
| MLA | Zhang, ZL,et al."Amorphous silicon-carbon nanospheres synthesized by chemical vapor deposition using cheap methyltrichlorosilane as improved anode materials for Li-ion batteries".NANOSCALE 5.12(2013):5384. |
入库方式： OAI收割
来源：物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。