Research on fracture behavior of a Cr coating/original steel substrate material under thermal fatigue loading
文献类型：会议论文
| 作者 | Yang BQ(杨班权); Chen GN(陈光南) ; Du J; Chen XJ(陈学军); Sun WH; Chen HQ; Pan JW; Chen Y
|
| 出版日期 | 2014 |
| 会议名称 | 2nd International Conference on Mechanical Engineering, Materials Science and Civil Engineering, ICMEMSCE 2013 |
| 会议日期 | OCT 25-26, 2013 |
| 会议地点 | Beijing, China |
| 卷号 | 470 |
| 页码 | 146-149 |
| 通讯作者 | 杨班权 |
| 中文摘要 | The facture behavior of a chromium (Cr) coating/ original steel substrate material was investigated in this work. The results presented in this work show the crack density of the Cr coating on the substrate increases with the increase of the thermal fatigue times, and the failure process and modes of the Cr coating /original steel substrate system can be described as follows: Firstly, the micro-cracks of the coating grew and interconnected as the thermal fatigue time increased. Secondly, the "pocket" cracking at the coating and the substrate interface occurred, and the main cracks of the coating formed. Finally, the spallation or (and) collapse of the coating occurred. |
| 收录类别 | EI |
| 合作状况 | 国内 |
| 产权排序 | [Yang Ban-Quan1;Chen Guang-Nan2;Du Jun3;Chen Xue-Jun4;Sun Wei-Hai1;Chen Hong-Qian1;Pan Jing-Wen1;Chen Ying1] 1 Division of Engineering Mechanics, Department of Mechanical Engineering, Academy of Armored Force Engineering, No. 21, Du-Jia-Kan, Chang-Xin-Dian, Beijing 100072, China; 2 Laboratory of surface modification, Institute of mechanics, Chinese Academy of Sciences, No. 15 Bei-si-huan-xi Road, Beijing 100190, China; 3 National Key Laboratory for Remanufacturing, Academy of Armored Force Engineering, No 21, Du-Jia-Kan, Chang-Xin-Dian, Beijing 100072, China; 4 School of Applied Sciences, University of Science and Technology Beijing, No. 30 Xue-Yuan Road, Beijing 100083, China |
| 会议网址 | http://dx.doi.org/10.4028/www.scientific.net/AMM.470.146 |
| 会议录 | Mechanical Engineering, Materials Science and Civil Engineering II
 |
| 会议录出版者 | TRANS TECH PUBLICATIONS LTD, ZURICH-DURNTEN |
| 语种 | 英语 |
| ISSN号 | 1660-9336 |
| ISBN号 | 9783037859612 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/48264]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 推荐引用方式 GB/T 7714 | Yang BQ,Chen GN,Du J,et al. Research on fracture behavior of a Cr coating/original steel substrate material under thermal fatigue loading[C]. 见:2nd International Conference on Mechanical Engineering, Materials Science and Civil Engineering, ICMEMSCE 2013. Beijing, China. OCT 25-26, 2013.http://dx.doi.org/10.4028/www.scientific.net/AMM.470.146. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。