Adhesion Behavior of Thermal Barrier Coating on Nickel Alloy in the Bullet Shock Testing
文献类型：会议论文
| 作者 | Zhang K(张坤) ; He LR(何伶荣); Peng Q(彭青); Wu CW(吴臣武); Chen GN(陈光南); Zhang K(张坤); Zhang K(张坤)
|
| 出版日期 | 2013 |
| 会议名称 | 20th Congress of International Federation for Heat Treatment and Surface Engineering |
| 会议日期 | OCT 23-25, 2012 |
| 会议地点 | Beijing, China |
| 通讯作者邮箱 | kzhang@imech.ac.cn |
| 关键词 | thermal barrier coatings adhesion metallography shock testing |
| 卷号 | 50 |
| 页码 | 139-144 |
| 通讯作者 | 张坤 |
| 中文摘要 | This paper applies bullet to induce shock wave and detects the adhesion behavior of multiple interfaces in typical thermal barrier coating system. Post-shock metallography examination is carried out to show the real characteristic of interface delamination. A finite element-based acoustic wave mechanics simulation is conducted to calculate the stress history. It is found that delamination can occur in every interface, depending on bullet velocity and stress feature. An interesting phenomenon of the failure at multiple interfaces during a single shot needs to be paid more attention in the future. |
| 产权排序 | [Zhang, Kun1; He, Lingrong2; Peng, Qing1; Wu, Chenwu1; Chen, Guangnan1] 1. Institute of Mechanics, Chinese Academy of Sciences, Beijing 100190, P.R. China; 2. No. 7801 Institute of China Aerospace Science and Industry Corporation, Changsha 410205, P.R. China |
| 会议网址 | http://dx.doi.org/10.1016/j.phpro.2013.11.023 |
| 会议录 | PHYSICS PROCEDIA
 |
| 会议录出版者 | ELSEVIER SCIENCE BV |
| 学科主题 | 制造工艺力学 |
| 语种 | 英语 |
| ISSN号 | 1875-3892 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/48339]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 通讯作者 | Zhang K(张坤); Zhang K(张坤) |
| 推荐引用方式 GB/T 7714 | Zhang K,He LR,Peng Q,et al. Adhesion Behavior of Thermal Barrier Coating on Nickel Alloy in the Bullet Shock Testing[C]. 见:20th Congress of International Federation for Heat Treatment and Surface Engineering. Beijing, China. OCT 23-25, 2012.http://dx.doi.org/10.1016/j.phpro.2013.11.023. |