Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture
文献类型：期刊论文
| 作者 | Xing RB ; Ye TL ; Ding Y ; Ding ZC ; Ma DG ; Han YC |
| 刊名 | chinese journal of chemistry
 |
| 出版日期 | 2013 |
| 卷号 | 31期号:11页码:1449-1454 |
| 关键词 | DIODES DISPLAYS MATRIX DEVICES DROPS |
| ISSN号 | 1614-7065 |
| 通讯作者 | han yc |
| 中文摘要 | in this paper, thickness uniformity of poly(9,9-di-n-octylfluorene) films patterned by inkjet printing was improved by the use of solvent mixtures (a solvent with higher volatility, higher surface energy and lower viscosity, with another solvent with lower volatility, lower surface energy and higher viscosity). the average thickness of inkjet printed poly(9,9-di-n-octylfluorene) films was increased from ca. 30 nm to ca. 100 nm when solvent mixtures were used instead of pure chlorobenzene. more flat pfo films were formed instead of the original films with concave-lens like cross-section formed by coffee ring effect. this improvement was explained by combination of intense marangoni flow at early drying process and weak complementary flow at the later drying process formed in the solvent mixture. patterned poly(9,9-di-n-octylfluorene) films were used for fabrication of electroluminescence devices with improved electronic property. array of pixels with about 80% effective light-emitting area was obtained. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000330180700013 |
| 公开日期 | 2014-04-15 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/49490]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Xing RB,Ye TL,Ding Y,et al. Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture[J]. chinese journal of chemistry,2013,31(11):1449-1454. |
| APA | Xing RB,Ye TL,Ding Y,Ding ZC,Ma DG,&Han YC.(2013).Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture.chinese journal of chemistry,31(11),1449-1454. |
| MLA | Xing RB,et al."Thickness Uniformity Adjustment of Inkjet Printed Light-emitting Polymer Films by Solvent Mixture".chinese journal of chemistry 31.11(2013):1449-1454. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。